A ductile hot-rolled steel bar has a minimum yield strength in tension and compression of 350 MPa. Using the distortion-energy and maximum-shear-stress theories determine the factors of safety for the following plane stress states:
(a) σx = 100 MPa, σy = 100 MPa
(b) σx = 100 MPa, σy = 50 MPa
(c) σx = 100 MPa, τxy = −75 MPa
(d) σx = −50 MPa, σy = −75 MPa τxy = −50 MPa
(e) σx = 100 MPa, σy = 20 MPa τxy = −20 MPa
(a)
The factor of the safety using maximum shear stress theory.
The factor of the safety using maximum distortion energy theory.
If
Answer to Problem 1P
The factor of the safety using maximum shear stress theory is
The factor of the safety using maximum distortion energy theory is
Explanation of Solution
Write the expression for the maximum principle stress.
Here, the normal stress in x direction is
Write the expression for the minimum principle stress.
Here, the normal stress in x direction is
Write the expression for the factor of the safety for MSST.
Here, the yield strength of the material in tension is
Write the expression for the factor of the safety for MDET.
Here, the yield strength of the material in tension is
Conclusion:
Substitute
Substitute
The maximum value from
Substitute
Thus, the factor of the safety using maximum shear stress theory is
Substitute
Thus the factor of the safety using maximum distortion energy theory is
(b)
The factor of the safety using maximum shear stress theory.
The factor of the safety using maximum distortion energy theory.
If
Answer to Problem 1P
The factor of the safety using maximum shear stress theory is
The factor of the safety using maximum distortion energy theory is
Explanation of Solution
Conclusion:
Substitute
Substitute
The maximum value between
Substitute
The factor of the safety using maximum shear stress theory is
Substitute
Thus, the factor of the safety using maximum distortion energy theory is
(c)
The factor of the safety using maximum shear stress theory.
The factor of the safety using maximum distortion energy theory.
If
Answer to Problem 1P
The factor of the safety using maximum shear stress theory is
The factor of the safety using maximum distortion energy theory is
Explanation of Solution
Conclusion:
Substitute
Substitute
The maximum value between
Substitute
Thus, the factor of the safety using maximum shear stress theory is
Substitute
Thus, the factor of the safety using maximum distortion energy theory is
(d)
The factor of the safety using maximum shear stress theory.
The factor of the safety using maximum distortion energy theory.
If
Answer to Problem 1P
The factor of the safety using maximum shear stress theory is
The factor of the safety using maximum distortion energy theory is
Explanation of Solution
Conclusion:
Substitute
Substitute
Calculate
The maximum values among
Substitute
Thus, the factor of the safety using maximum shear stress theory is
Substitute
Thus, the factor of the safety using maximum distortion energy theory is
(e)
The factor of the safety using maximum shear stress theory.
The factor of the safety using maximum distortion energy theory.
If
Answer to Problem 1P
The factor of the safety using maximum shear stress theory is
The factor of the safety using maximum distortion energy theory is
Explanation of Solution
Conclusion:
Substitute
Substitute
Calculate
The maximum values among
Substitute
Thus, the factor of the safety using maximum shear stress theory is
Substitute
Thus, the factor of the safety using maximum distortion energy theory is
Want to see more full solutions like this?
Chapter 5 Solutions
Shigley's Mechanical Engineering Design (McGraw-Hill Series in Mechanical Engineering)
- (a) Solve part (a) of the preceding problem if the pressure is 8.5 psi, the diameter is 10 in., the wall thickness is 0,05 in., the modulus of elasticity is 200 psi, and Poisson's ratio is 0.48. (b) If the strain must be limited to 1.01, find the maximum acceptable inflation pressurearrow_forwardTwo sections of steel drill pipe, joined by bolted flange plates at Ä are being tested to assess the adequacy of both the pipes. In the test, the pipe structure is fixed at A, a concentrated torque of 500 kN - m is applied at x = 0.5 m, and uniformly distributed torque intensity t1= 250 kN m/m is applied on pipe BC. Both pipes have the same inner diameter = 200 mm. Pipe AB has thickness tAB=15 mm, while pipe BC has thickness TBC= 12 mm. Find the maximum shear stress and maximum twist of the pipe and their locations along the pipe. Assume G = 75 GPa.arrow_forwardSolve the preceding problem if the diameter is 480 mm, the pressure is 20 MPa, the yield stress in tension is 975 MPa, the yield stress in shear is 460 MPa, the factor of safety is 2,75, the modulus of elasticity is 210 GPa, Poissorfs ratio is 0.28, and the normal strain must not exceed 1190 x 10" . For part (b), assume that the tank thickness is 8 mm and the measured normal strain is 990 x 10~ .arrow_forward
- The strength-to-weight ratio of a structural material is defined as its load-carrying capacity divided by its weight. For materials in tension, use a characteristic tensile stress obtained from a stress-strain curve as a measure of strength. For instance, either the yield stress or the ultimate stress could be used, depending upon the particular application. Thus, the strength-to-weight ratio RS/Wfor a material in tension is defined as Rs/w= in which a is the characteristic stress and 7 is the weight density. Note that the ratio has units of length. Using the ultimate stress Uas the strength parameter, calculate the strength-to-weight ratio (in units of meters) for each of the following materials: aluminum alloy 606I-T6, Douglas fir (in bending}, nylon. structural steel ASTM-A57.2, and a titanium alloy. Obtain the material properties from Tables [-1 and 1-3 of Appendix I. When a range of values is given in a table, use the average value.arrow_forwardA wine of length L = 4 ft and diameter d = 0.125 in. is stretched by tensile forces P = 600 lb. The wire is made of a copper alloy having a stress-strain relationship that may be described mathematically by =18,0001+30000.03(=ksi) in which is nondimensional and has units of kips per square inch (ksi). (a) Construct a stress-strain diagram for the material. (bj Determine the elongation, of the wire due to the Forces P. (c) IF the forces are removed, what is the permanent set of the bar? (d) If the forces are applied again, what is the proportional limit?arrow_forwardA ductile hot-rolled steel bar has a minimum yield strength in tension and compression of Syt = 50 kpsi and Syc = 65 kpsi. Using the ductile Coulomb-Mohr theory, determine the factor of safety for the states of plane stress. 0x = 35 kpsi, and oy = 20 kpsi, Txy = 0 Submit your answer in 4 significant digits. (25 points)arrow_forward
- 1. A ductile hot-rolled steel bar has a yield strength in tension and compression of 350 MPa. Using the distortion-energy and maximum-shear-stress theories, determine the factors of safety for the following plane stress state: 75 MPa 50 MPa 50 MPaarrow_forwardA pressure vessel is exposed to a combination of loads as shown below. The vessel (diameter 100 mm) has a wall thickness of 3 mm. Address the following: (a) If the yield strength of the material is 144 MPa, determine the largest tension force P with respect to a factor of safety of 2 applied to the distortional energy theory. (b) If the applied torque and tension load were removed, determine the minimum wall thickness using a factor of safety of 1.75 with respect to the distortional energy theory. Illustrate you results using an appropriate yield envelope. p = 3.5 MPa T = 450 N-m show all wah Parrow_forwardThe 0.06R (mm)-diameter bar is made of a brittle material with the ultimate strengths of 0.15R MPa in tension and 0.25R MPa in compression. The bar carries a bending moment and a torque, both of magnitude M. (a) Use the maximum normal stress theory to find the largest value of M that does not cause rupture. (b) Is the value of M found in Part (a) safe according to Mohr’s theory of failure? Note R=993arrow_forward
- A pressure vessel is exposed to a combination of loads as shown below. The vessel (diameter 100 mm) has a wall thickness of 3 mm. Address the following: (a) If the yield strength of the material is 144 MPa, determine the largest tension force P with respect to a factor of safety of 2 applied to the distortional energy theory. (b) If the applied torque and tension load were removed, determine the minimum wall thickness using a factor of safety of 1.75 with respect to the distortional energy theory. Illustrate you results using an appropriate yield envelope. p = 3.5 MPa T = 450 N-m P Tarrow_forwardA brittle material has the properties Sut = 30kpsi and Sue = 90kpsi. Determine the factor of safety for the following states of stresses using; Brittle Coulomb Mohr Theory Modified Mohr 1 Theory (a) ox = 20kpsi,Oy = (b) o = 15kpsi,o, = -25kpsi (c) ox = 10kpsi,0y = -40kpsi (d) o, = -20kpsi,o, = -20kpsi, txy = -40 10kpsi, ty = -15kpsi (1) Draw the stress element (11) Plot the failure diagram in the o-plane (III) Estimate the factor of safetyarrow_forwardA circular rod of length 18 cm and diameter 5 mm is made of grade 1045 grade steel. a. Calculate the stress and strain in the rod, and its extension, when it is subjected to 7 kN of tension. (Express your answers using three significant figures.) |MPa E = x10-4 (Express your answer using whole numbers.) AL = | pm b. At what force would the rod begin to yield? (Express your answer using three significant figures.) F = |kN c. By what amount would the rod have to be stretched beyond its original length in order to yield? (Express your answer using whole numbers.) AL = umarrow_forward
- Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning