Question
Chapter 2, Problem 2.59P
To determine
The shear stress and the normal stress acting on fracture surface.
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
A 200mm long rod with a diameter of 50mm is loaded with a 4kN weight. The rod final length 201.314mm and final diameter 42mm the load at fracture is 2.5kN and the maximum load is 3.5KN.
1. Calculate the stress
2. Calculate the strain
3. Calculate limit of proportionality
A ceramic part for a jet engine has a yield
strength of 75,000 psi and a plane strain
fracture toughness of 5,000 psiVin. To be
sure that the part does not fail, we plan
to ensure that the maximum applied stress
is only one-third of the yield strength. We
use a nondestructive test that will detect
any internal faws greater than 0.05 in.
long. Assuming that f = 1.4, does our
nondestructive test have the required
sensitivity? Explain.
A manufacturine proorssthat unintention
An 820 MPa (145,000 psi) stress is applied to a specimen of 4341 steel alloy, which has a plane strain fracture toughness of 45MPa squareroot (m). If the greatest surface crack is 0.95 mm (0.03 in) long, will this specimen fracture as a result? Assume that the parameter Y is 1.22.
Chapter 2 Solutions
EBK MANUFACTURING PROCESSES FOR ENGINEE
Ch. 2 - Prob. 2.1QCh. 2 - Prob. 2.2QCh. 2 - Prob. 2.3QCh. 2 - Prob. 2.4QCh. 2 - Prob. 2.5QCh. 2 - Prob. 2.6QCh. 2 - Prob. 2.7QCh. 2 - Prob. 2.8QCh. 2 - Prob. 2.9QCh. 2 - Prob. 2.10Q
Ch. 2 - Prob. 2.11QCh. 2 - Prob. 2.12QCh. 2 - Prob. 2.13QCh. 2 - Prob. 2.14QCh. 2 - Prob. 2.15QCh. 2 - Prob. 2.16QCh. 2 - Prob. 2.17QCh. 2 - Prob. 2.18QCh. 2 - Prob. 2.19QCh. 2 - Prob. 2.20QCh. 2 - Prob. 2.21QCh. 2 - Prob. 2.22QCh. 2 - Prob. 2.23QCh. 2 - Prob. 2.24QCh. 2 - Prob. 2.25QCh. 2 - Prob. 2.26QCh. 2 - Prob. 2.27QCh. 2 - Prob. 2.28QCh. 2 - Prob. 2.29QCh. 2 - Prob. 2.30QCh. 2 - Prob. 2.31QCh. 2 - Prob. 2.32QCh. 2 - Prob. 2.33QCh. 2 - Prob. 2.34QCh. 2 - Prob. 2.35QCh. 2 - Prob. 2.36QCh. 2 - Prob. 2.37QCh. 2 - Prob. 2.38QCh. 2 - Prob. 2.39QCh. 2 - Prob. 2.40QCh. 2 - Prob. 2.41QCh. 2 - Prob. 2.42QCh. 2 - Prob. 2.43QCh. 2 - Prob. 2.44QCh. 2 - Prob. 2.45QCh. 2 - Prob. 2.46QCh. 2 - Prob. 2.47QCh. 2 - Prob. 2.48QCh. 2 - Prob. 2.49PCh. 2 - Prob. 2.50PCh. 2 - Prob. 2.51PCh. 2 - Prob. 2.52PCh. 2 - Prob. 2.53PCh. 2 - Prob. 2.54PCh. 2 - Prob. 2.55PCh. 2 - Prob. 2.56PCh. 2 - Prob. 2.57PCh. 2 - Prob. 2.58PCh. 2 - Prob. 2.59PCh. 2 - Prob. 2.60PCh. 2 - Prob. 2.61PCh. 2 - Prob. 2.62PCh. 2 - Prob. 2.63PCh. 2 - Prob. 2.64PCh. 2 - Prob. 2.65PCh. 2 - Prob. 2.66PCh. 2 - Prob. 2.67PCh. 2 - Prob. 2.68PCh. 2 - Prob. 2.69PCh. 2 - Prob. 2.70PCh. 2 - Prob. 2.71PCh. 2 - Prob. 2.72PCh. 2 - Prob. 2.73PCh. 2 - Prob. 2.74PCh. 2 - Prob. 2.75PCh. 2 - Prob. 2.76PCh. 2 - Prob. 2.78PCh. 2 - Prob. 2.79PCh. 2 - Prob. 2.80PCh. 2 - Prob. 2.81PCh. 2 - Prob. 2.82PCh. 2 - Prob. 2.83PCh. 2 - Prob. 2.84PCh. 2 - Prob. 2.85PCh. 2 - Prob. 2.86PCh. 2 - Prob. 2.87PCh. 2 - Prob. 2.88PCh. 2 - Prob. 2.89PCh. 2 - Prob. 2.90PCh. 2 - Prob. 2.91PCh. 2 - Prob. 2.92PCh. 2 - Prob. 2.93PCh. 2 - Prob. 2.94PCh. 2 - Prob. 2.95PCh. 2 - Prob. 2.96PCh. 2 - Prob. 2.97PCh. 2 - Prob. 2.98PCh. 2 - Prob. 2.99PCh. 2 - Prob. 2.100PCh. 2 - Prob. 2.101P
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- Consider a solid bar with 1.00 in diameter subjected to a bending moment, M, and a twisting moment, T, with equal magnitudes, so that M = T. M a) If the bar is made of a brittle material that fails in uniaxial tension at 6000 psi, what is the minimum value of M and T that would cause brittle failure? Make a sketch of the bar and show the orientation of the fracture plane relative to the axial direction of the bar. b) If the bar is made of a ductile material with yield stress of 36000 psi, what is the minimum value of M and T that would cause yielding? Assume von-Mises theory. Hint: Start by determining the state of stress at a point on the top of the bar.arrow_forwardA specimen of steel 20 mm diameter with a gauge length of 200 mm is tested to destruction. It has an extension of 0.25 mm under a load of 80 kN and the load at elastic limit is 102 kN. The maximum load is 130 kN. The total extension at fracture is 56 mm and diameter at neck is 15 mm. Find (i)The stress at elastic limit.(ii) Young’s modulus.(iii) Percentage elongation. (iv)Percentage reduction in area. (v)Ultimate tensile stress.arrow_forwardcylindrical specimen of steel having an original diameter of 0.505 in. is tensile tested to fracture and found to have an engineering fracture strength of 67,000 psi. If its cross-sectional diameter at fracture is 0.422 in, determine:(a) The ductility in terms of percent reduction in area(b) The true stress at fracturearrow_forward
- How can I solve for the %0.2 offset strain and the calculated stress? Original diameter : 6mm Original length : 30mm Fracture diameter : 4.54mmarrow_forwardA cast iron cylinder has outside and inside diameter 200mm and 125mmrespectively. If the ultimate strength of cast iron is 150MPa calculate according to each of the following theories of failure the internal pressure that will cause fracture.(a) Maximum principal stress theory. (b) Maximum principal strain theory. (c) Maximum strain energy theory. Assume no longitudinal stress in the cylinder. Which of the results obtained you consider should be applied to this case. Take:µ = 0.25, σU = 150MPa. Ans: (a) 65.73MPa. (b) 59.24MPa, (c) 55.33MPa.arrow_forwardDetermine the fracture load (in N) of a copper specimen subjected to a tensile load if the breaking stress is 555 N/mm2 and the cross-sectional area at fracture is 6 mm².arrow_forward
- Consider a cylindrical metal 16 mm in diameter and 70 mm long is pulled in tension. It is known that the yield strength and elastic (Young's) Modulus of the material are 350 MPa and 200 GPa, respectively, and its Poisson's Ratio is 0.3. (e) Calculate the ductility in terms of % E.L. if the length of the specimen at the fracture point is 76.0 mm.arrow_forwardA three-point transverse bending test was performed on a glass specimen having a square cross-section of 18.5 mm length on each edge. The specimen fractured at a load of 4530 N when the distance between support points was 42 mm. A second test is to be performed on another specimen of this same glass material, but one that has a circular cross-section. What minimum specimen diameter is required to ensure that fracture will not occur when a load of 3480 N is applied? Assume that the support separation is maintained at 42 mm. mmarrow_forwardA metallic rod with an initial diameter of 10 mm and an initial length of 50 mm is subjected to the tensile test. After the fracture, the final length was measured as 51.8 mm, and the final diameter was measured as 9.5 mm.(a) Calculate modulus of elasticity, ultimate tensile strength, elongation at fracture in %,reduction of area in %, true stress at maximum load, true strain at maximum load, strain hardening exponent, strength coefficient.?arrow_forward
- A cylindrical metal specimen having an original diameter of 12.8 mm (0.505 in.) and gauge length of m (2.000 in.) is pulled in tension until fracture occurs. The diameter at the point of fracture is 6.60 mm (0.260 in.), and the fractured gauge length is 72.14 mm (2.840 in.). Calculate the ductility in terms of percent reduction in area and percent elongation.arrow_forward4. The gauge of the Impact Testing Apparatus shows 52 divisions. Calculate the amount of energy adsorbed per unit surface prior to fracture. Remeber that 1 division corresponds to 2 Joules and the fracture surface is 8 mm x 10 mm, not 10 mm x 10 mm.arrow_forwardAn annealed-steel specimen has a 0.750 in. diameter and a 12.000 in. gage length. Maximum load is reached at 60,000 lbs and fracture occurs at 30,000 Ibs. For this steel, E= 360 x 10° psi. (a) Draw a sketch of stress-strain diagram for a typical steel in tension? (b) What is the ultimate tensile strength (UTS)? (c) Why does fracture occur at a lower load than the maximum load? (d) What is the elongation when a tensile stress of 30,000 psi is applied? A 400-mm-long rod with a diameter of 4.5 mm is loaded with a 5000-N weight. If the diameter decreases to 3.5 mm, compute the final length of the rod. 3. 4. A steel rod 1.5 m long and 75 mm x 75 mm in cross-section is subjected to a tensile force of 160 kN. Determine the elongation of the rod, if modulus of elasticity for the rod material is 900 GPa. 5. A hollow cylinder 4.5 m long has an outside diameter of 80 mm and inside diameter of 60 mm. If the cylinder is carrying a load of 75 kN, find the stress in the cylinder. Also find the…arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Material Properties 101; Author: Real Engineering;https://www.youtube.com/watch?v=BHZALtqAjeM;License: Standard YouTube License, CC-BY