(a) How is raw pig iron extracted from iron oxide ores? (b) Write a typical chemical reaction for the reduction of iron oxide (Fe2O3) by carbon monoxide to produce iron. (c) Describe the basic oxygen process for converting pig iron into steel.
(a)
How is raw pig iron extracted from iron oxide ores?
Explanation of Solution
Raw pig iron is usually extracted from ores of iron oxide in a blast furnace in the presence of reducing agent. The typical reducing agent used in the blast furnace is coke. The produced pig iron contains nearly 4% of carbon.
(b)
Write a typical chemical reaction for the reduction of iron oxide by carbon monoxide to produce iron.
Explanation of Solution
Write chemical reaction for the reduction of iron oxide by carbon monoxide.
Here, iron oxide is
(c)
Describe the basic oxygen process for converting pig iron into steel.
Explanation of Solution
In the basic oxygen process, pig iron is changed into steel by the process of oxidation in a convertor of refractory-lined type. A lance of oxygen insert gives pure oxygen to perform a bathing of molten pig iron and scrapping of steel.
The formed iron oxide then reacts with the carbon in the steel to produce carbon monoxide.
Want to see more full solutions like this?
Chapter 9 Solutions
Foundations of Materials Science and Engineering
- rams A copper-nickel alloy of composition 75 wt% Ni-25 wt% Cu is slowly heated from a temperature of 1300°C (1573). (a) At what temperature does the first liquid phase form? (b) What is the composition of this liquid phase? T(°C) 1600 (c) At what temperature does complete melting of the alloy occur? (d) What is the composition of the last solid remaining prior to complete melting? 1500 1400 1300 1200 1100 1000 17 / 17 0 L (liquid) 20 liquidus + a solidus 100% 40 α (FCC solid solution) 60 80 100 wt% Ni 17arrow_forwardQuestion: 4 A sheet of copper is exposed to oxygen at 1000°C. After 100 h, 0.245 g of copper are lost per cm' of surface area; after 250 h, 0.385 g/ cm² are lost; and after 500 h, 0.560 g/ em are lost. i. Determine whether oxidation is parabolic, linear, or logarithmic ii. Calculate the time required for a 0.76-cm sheet of copper to be completely oxidized. The sheet of copper is oxidized from both sides.arrow_forwardDraw thermal equilibrium diagram for the binary alloy system (Si-Au), from the following data:- a- Silicon melts at 1414 °C, and gold melts at 1064 °C. b-Eutectic is formed at 360°C containing 20 Wt% Si -80 Wt% Au, and identify all phases are present in the diagram c-Determine the amount of each phase for the alloy which consist of 60 Wt% Si- 40Wt % Au at 1200 °C and 800 °C ,then determine the amount of eutectic at 200 °C?arrow_forward
- Consider 2.4 kg of a 99.7 wt% Fe-0,3 wt% C alloy that is cooled to a temperature just below the eutectoid. The iron-iron carbide phase (a) How many kilograms of proeutectoid ferrite form? kg (b) How many kilograms of eutectoid ferrite form? kg (c) How many kilograms of cementite form? kgarrow_forwardConsider de-oxidation by the addition of ferromanganese (60 percent Mn) to molten steel at 1600°C.The initial oxygen content is 0.04 wt%. It has to be brought down to 0.02 wt%. Calculate the quantity of ferromanganese required per tonne of steel. The manganese content of steel before de- oxidation is 0.1 wt%. (MnO) + [Fe] = [Mn] + (FeO) Given: K Mn at 1873 K = 0.4 K Fe-Mn at 1873 K = 0.156 Assumptions: Fe and Mn form ideal solutionsarrow_forwardIron (Fe) undergoes an allotropic transformation at 912°C: upon heating from a BCC (α phase) to an FCC (γ phase). Accompanying this transformation is a change in the atomic radius of Fe—from RBCC = 0.12584 nm to RFCC = 0.12894 nm—and, in addition, a change in density (and volume). Compute the percentage volume change associated with this reaction. Indicate a decreasing volume by a negative number.arrow_forward
- The chemical composition of X38CrMoV5-3 steel is given in the table below. b) This steel is austenitized at 1050 ° C and hardened by giving water in oil (completely martensite structure has been formed and has a hardness of 57 HRC) and tempered at 510 ° C to reduce its hardness (54 HRC) and gain toughness. In addition, it is desired to harden the surface by nitration. In order to achieve the desired surface hardness, liquid nitration should be done at 600 ° C, gas nitration at 510 ° C and plasma nitration at 450 ° C. Which nitration method do you prefer? Why is that?arrow_forwardIn a binary Fe-Fe3C system, what is a transformation that occurs when cooling an austenistic mixture of 2% C by weight from 1100°C to below the eutectoid temperature? What is the microstructure, and how is it formed? What are the total and partial phases? Given:Eutectoid temperature=723°C; Eutectoid concentration=0.76% C; Limit concentration of ferrite=0.022%; Limiting concentration of cementite: 6.7%.arrow_forwardFor an Fe-0.35% C alloy, determine the composition and amount of each phase present at 726 ° C; and the composition and amount of each microconstituent present at 726 °C.arrow_forward
- In the present figure: compare between the alloy number 1 (0.4% C) and 2 (1.2% C) regarding: A. The expected mechanical properties of the two alloys (with explanation). B. .The range of applications for these alloys. C. The stages of annealing treatments Including: 1) Softening. 2) Spheroidizing. 3) Grain Size Reducing... 1 2 I p+ Fe,C a + parrow_forwardAnalyze the development of microstructure in Iron-Carbon alloys.arrow_forwardList the phase(s) that are present, the phase composition(s) and the weight fractions of the phase(s) for each of the following alloys:(a) 70 wt% Zn-30 wt% Cu at 300 C (b) 90 wt% Pb-10 wt% Sn at 325 C (c) 2.5 kg Cu and 5.0 kg Ag at 900 C (d) 37 lbm Pb and 6.5 lbm Mg at 500 Carrow_forward
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY