What are the characteristics of the surface of a ductile fracture of a metal?
The characteristic of a surface of a ductile fracture of a metal.
Explanation of Solution
When a material undergoes plastic deformation, ductile fracture occurs. The characteristics of a surface of a ductile fracture of a metal are listed below:
The below figure represents the ductile fracture of a specimen and the plot between stresss and strain of ductile material.
Figure-(1)
The point
Want to see more full solutions like this?
Chapter 7 Solutions
Foundations of Materials Science and Engineering
Additional Engineering Textbook Solutions
Fluid Mechanics: Fundamentals and Applications
Engineering Mechanics: Dynamics (14th Edition)
EBK FUNDAMENTALS OF THERMODYNAMICS, ENH
Machine Elements in Mechanical Design (6th Edition) (What's New in Trades & Technology)
Thermodynamics: An Engineering Approach
Shigley's Mechanical Engineering Design (McGraw-Hill Series in Mechanical Engineering)
- Question 3: A specimen of a 4340 steel alloy, having a plane strain fracture toughness of 45 MPalm a yield strength of 800 MPa, and a tensile strength of 1100 MPa, is exposed to a stress of 1000 MPa. Will this specimen experience fracture if it is known that the largest surface crack is 0.75 mm long? Why or why not? Assume that the parameter Y has a value of 1.0.arrow_forward(b) A 12.8 mm diameter rod and gauge length of 40 mm of aluminum alloy is pulled to failure in a tensile test. If final diameter of the rod fracture surface is 10.8 mm and fracture gauge is 64 mm, answer the following: (i) Calculate the ductility in percent reduction in area of the sample. (ii) Explain how ductility is related to the toughness of the material.arrow_forwardDescribe the appearance of a fatigue fracture?arrow_forward
- On what does a tensile fracture generally depend?arrow_forwardWhy is the prediction of the tensile fracture of a brittle material is difficult to predict?arrow_forwardA brass specimen of the circular cross-section is fractured at 147 kN force and the final length of the specimen at fracture is 46 mm. The fracture strength of the specimen is found to be 79 kN/mm?. The percentage of elongation of the specimen is 41 %. Determine the following (i) Diameter of the specimen, ( ii) Initial length of the specimen,( iii) Stress under an elastic load of 13 kN, (* iv) Young's Modulus if the elongation is 1.3 mm at 13 kN ( (v) Final diameter if the percentage of reduction in area is 29 %. ( Young's Modulus of the Specimen (in N/mm²) Final Area of the Specimen at Fracture (in mm) Final Diameter of the Specimen after Fracture (in mm)arrow_forward
- What is the magnitude of the maximum stress that exists at the tip of an internal crack having a radius of curvature of 1.9 x 10" mm and a crack length of 3.8 x 10 mm when a tensile stress of 140 MPa is applied? 4. 5. A ceramic matrix composite contains internal flaws as large as 0.001 cm in length. The plane strain fracture toughness of the composite is 45 and the tensile strength is 550 MPa. Will the flaw cause the composite to fail before the tensile strength is reached? Assume that Y 1 A cylindrical rod 500 mm long, having a diameter of 12.7 mm, is to be subjected to a tensile load. If the rod is to experience neither plastic deformation nor an elongation of more than 1.3 mm. when the applied load is 29,000 N, which of the four met ls or alloys listed below are possible cardidates? Justify your choice(s). Materia! Modulus of Yield Tensiie Strength (MPa) Elasticity(GPa) Strength(MPa) Aluminium alloy 70 255 420 Brass alloy 100 345 420 Сopper 110 210arrow_forwardA component made of 7075-T6 aluminum alloy has an edge crack of 1.4 mm in length. Plane strain fracture toughness of this alloy is given as 27 MPavm. Geometrical factor of the crack is given as 1.2.| (a) If this component is subjected to uniaxial tensile stress of 380 MPa, determine whether sudden brittle fracture will occur or not. (b) Calculate the maximum allowable crack size for this component in order not to be failed in brittle manner under a stress of 1000 MPa.arrow_forwardUnder what conditions may a ductile material undergo a brittle fracture?arrow_forward
- What is the difference in appearance between ductile & brittle fractures?arrow_forwardA three-point bending test was performed on an aluminum oxide specimen having a circular cross section of radius = 5 mm, the specimen fractured at a load of 1400 N when the distance between the support points L = 100 mm. Another test is to be performed on a specimen of this same material, but one that has a square cross section of 12 mm on each edge. At what load would you expect this specimen to fracture if L = 50 mm? i need clear ans by hand and solve very very fast in 20 min and thank you DYBALARI |arrow_forwardWhat is the cause of the fracture of a brittle material?arrow_forward
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY