The expression for extrusion pressure.
Explanation of Solution
The figure (1) demonstrate the forces on the specimen in a wire drawing process.
Figure (1)
The expression for the equilibrium in x direction can be given as,
Here, pressure along the die contact is
After expanding the above equation,
Further solving the above equation,
Expression for pressure
Substituting the value of
Integration of equation (2) for boundary condition
Simplifying the above equation,
The expression for the ratio of area,
Substituting the above value in the equation (3),
For,
Conclusion:
Therefore, the equation is
Want to see more full solutions like this?
Chapter 6 Solutions
EBK MANUFACTURING PROCESSES FOR ENGINEE
- 2. A metal alloy has been tested in a tensile test with the following results for the flow curve parameters: strength coefficient = 620.5 MPa and strain-hardening exponent 0.26. The same metal is now tested in a compression test in which the starting height of the specimen = 62.5 mm and its diameter = 25 mm. Assuming that the cross section increases uniformly, determine the load required to compress the specimen to a height of (a) 50 mm and (b) 37.5 mm. 3. The starting length of a shaft is 25.00 mm. This shaft is to be inserted into a hole in an expansion fit assembly operation. To be readily inserted, the shaft must be reduced in length by cooling. Determine the temperature to which the shaft must be reduced from room temperature (20° C) in order to reduce its length to 24.98 mm. Refer to the Table below. Volumetric properties in U.S. customary units for selected engineering materials. Coefficient of Thermal Expansion, a Density, p Ib/in Melting Point, T Material g/cm C'x 10 F'x 10 6…arrow_forwardA loading causes the block to deform into the dashed shape. Explain how to determine the strains PAB, PAC, PBC, (gA)xy. The angles and distances between all lettered points are known.arrow_forward2. A metal alloy has been tested in a tensile test with the following results for the flow curve parameters: strength coefficient = 620.5 MPa and strain-hardening exponent = 0.26. The same metal is now tested in a compression test in which the starting height of the specimen = 62.5 mm and its diameter 25 mm. Assuming that the cross section increases uniformly, determine the load required to compress the specimen to a height of (a) 50 mm and (b) 37.5 mm.arrow_forward
- 1 %AV l. 1:Y0 A docs.google.com/forms/d/e مختبر ميكانيك المواد Why used two equipment in shear force and bending moment experiment (one for ?S.F and the other to B.M) إجابتك What is the relationship between the ?distance from neutral axis and stress إجابتك Explain in steps with detail, how can find the ?Young's modulus for any unknown beam إجابتك What is the meaning of + S.F, -S.F, +B.M and ?- B.M إجابتك صفحة 4 من 5 IIarrow_forwardSIMPLE STRAINarrow_forwardWhat is the linear variation in the shear strain?arrow_forward
- [Problem 4] Show that the following strain components are the solutions of a problem in elasticity. E, = 2.xy', E, = -6.xy', E, = 2.x' +x'y-y Where & is defined as the small strain component. urgent solution.please explain properly. will surely upvotearrow_forwardThe rectangular plate is deformed into the shape shown by the dashed lines. Suppose that a = 330 mm and b = 370 mm. (Figure 1) PART A) Determine the average normal strain along diagonal BD.Express your answer using three significant figures. PART B) Determine the average shear strain γxy at corner B relative to the x, y axes..Express your answer to three significant figures and include the appropriate units.arrow_forwardThe relationship between true strain (ɛ-) and engineering strain (ɛ) in a uniaxial tension test is given as (a) & = In (1 + &7) (c) &7= In (1+ E) (b) ɛg = In (1- E) (d)= in (1- E) %3D %3Darrow_forward
- Tensile test is a method to investigate the elasticity of a material. A test specimen is placed between two clamps and these clamps will move in opposite directions, hence straining the test specimen. This experiment will yield a stress-strain curve that shows each of the stages of the specimen for every load is applied. With an aid of sketching diagrams, describe the stages that the specimen experiences before it breaks, and relate it with the stress-strain curve. It is expected that each stage comes with a sketching of the specimen and explanation of the current stage.arrow_forwardTensile test specimens are extracted from the "X" and "y" directions of a rolled sheet of metal. "x" is the rolling direction, "y" is transverse to the rolling direction, and "z" is in the thickness direction. Both specimens were pulled to a longitudinal strain = 0.15 strain. For the sample in the x-direction, the width strain was measured to be ew= -0.0923 at that instant. For the sample in the y-direction, the width strain was measured to be gw=-0.1000 at that instant. The yield strength of the x-direction specimen was 50 kpsi and the yield strength of the y-direction specimen was 52 kpsi. Determine the strain ratio for the x direction tensile test specimen. Determine the strain ratio for the y-direction tensile test specimen. Determine the expected yield strength in the z-direction. Give your answer in units of kpsi (just the number). If the sheet is plastically deformed in equal biaxial tension (a, = 0, to the point where & = 0.15, calculate the strain, 6, that would be expected.arrow_forward%9V li. M نقطتان )2( A tensile test is performed on a metal specimen, and it is found that a true plastic strain of 0.16 is produced when a true stress of 500 MPa is applied; for the same metal, the value of K is 825 MPa. Calculate the true strain that results from the application of a true stress of 600 * .MPa إضافة ملفarrow_forward
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY