Textbook Question
Chapter 1, Problem 13P
A fatigue test is performed on rotating beam specimens where, for each rotation cycle, the specimens experience tensile and compressive stresses of equal magnitude. The cycles-to-failure experience with 69 specimens of 5160H steel from 1.25-in hexagonal bar stock was as follows:
| L | 60 | 70 | 80 | 90 | 100 | 110 | 120 | 130 | 140 | 150 | 160 | 170 | 180 | 190 | 200 | 210 |
| f | 2 | 1 | 3 | 5 | 8 | 12 | 6 | 10 | 8 | 5 | 2 | 3 | 2 | 1 | 0 | 1 |
where L is the life in thousands of cycles, and f is the class frequency of failures.
- (a) Estimate the mean and standard deviation of the life for the population from which the sample was drawn.
- (b) Presuming the distribution is normal, how many specimens are predicted to fail at less than 115 kcycles?
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solution
Students have asked these similar questions
Q-3 The following creep data were taken on an aluminum alloy at 400°C (750°F)
and a constant stress of 25 MPa (3660 psi). Plot the data as strain versus time, then
determine the steady-state or minimum creep rate.
Time
Time
(min)
Strain
(min)
Strain
0.00
18
0.82
0.22
20
0.88
4
0.34
22
0.95
0.41
24
1.03
8
0.48
26
1.12
10
0.55
28
1.22
12
0.62
30
1.36
14
0.68
32
1.53
16
0.75
34
1.77
The following stress-strain curve was prepared based on a tensile test of a specimen that had a circular cross-section. The gage
diameter of the specimen was 0.25 inches and the gage length was 4 inches. The stress scale of the stress-strain diagram is
given with the factor a = 10 ksi. Estimate:
(a) The modulus of elasticity.
(b) The ultimate strength.
(c) The yield strength (0.2% offset).
(d) The percent elongation at fracture.
2013 Michael Swanbom
STRESS VS. STRAIN
BY NC SA
7a
bat
Sat
2at
at
0.05
STRAIN
0.01
0.04
0.06
0.08
0.02
0.03
0.07
0.09
STRESS
Given: Stress strain curve of 10 mm diameter and 1 m long ductile stainless-steel rod.
900
800
700
600
500
Mild
400
Stainless
300
200 -
100
0.1
0.2
0.3
0.4
Strain
0.5
0.6
0.7
Draw stress-strain curve for compression here
1. Label all points of significance on the stress strain curve
2. Draw the stress-strain curve for the rod in compression and label all points of significance.
3. What is the Young's modulus in tension? Assume .001 strain at 500 MPa
4. What is its Youngʻs modulus in compression?
5. What is the tensile yield strength of this rod using the 0.2% offset criteria?
6. What is the compressive yield strength of the rod?
7. What is force required to yield the rod?.
Show calculation:
8. What is the UTS of this rod?.
9. What is the force required to break the rod?
Show calculation:
10. What will be UCS of the rod?
Stress (MPa)
Chapter 1 Solutions
Shigley's Mechanical Engineering Design (McGraw-Hill Series in Mechanical Engineering)
Ch. 1 - Select a mechanical component from Part 3 of this...Ch. 1 - Select a mechanical component from Part 3 of this...Ch. 1 - Select an organization listed in Sec. 16, go to...Ch. 1 - Go to the Internet and connect to the NSPE website...Ch. 1 - Go to the Internet and connect to the NSPE website...Ch. 1 - Estimate how many times more expensive it is to...Ch. 1 - The costs to manufacture a part using methods A...Ch. 1 - A cylindrical part of diameter d is loaded by an...Ch. 1 - When one knows the true values x1 and x2 and has...Ch. 1 - Use the true values x1 = 7 and x2 = 8 (a)...
Ch. 1 - A solid circular rod of diameter d undergoes a...Ch. 1 - A fatigue test is performed on rotating beam...Ch. 1 - Determinations of the ultimate tensile strength...Ch. 1 - The lives of parts are often expressed as the...Ch. 1 - The tensile 0.2 percent offset yield strength of...Ch. 1 - A mechanical system comprises three subsystems in...Ch. 1 - From See. 3-12, the maximum shear stress in a...Ch. 1 - A round cold-drawn 1045 steel rod has a mean...Ch. 1 - A beam subjected to axial loading will experience...Ch. 1 - Three blocks A, B, and C and a grooved block D...Ch. 1 - The volume of a rectangular parallelepiped is...Ch. 1 - A pivot in a linkage has a pin in the figure whose...Ch. 1 - A circular cross section O ring has the dimensions...Ch. 1 - Prob. 25PCh. 1 - Prob. 26PCh. 1 - Prob. 27PCh. 1 - Prob. 28PCh. 1 - Convert the following to appropriate ips units:...Ch. 1 - Convert the following to appropriate SI units: (a)...Ch. 1 - Generally, final design results are rounded to or...Ch. 1 - Repeal Prob. 1-31 for the following: (a) = F/wt,...Ch. 1 - Repeat Prob. 131 for: (a) = F/A, where A = d2/4, F...
Additional Engineering Textbook Solutions
Find more solutions based on key concepts
17–1C A high-speed aircraft is cruising in still air. How does the temperature of air at the nose of the aircra...
Thermodynamics: An Engineering Approach
The triple jump is a track-and-field event in which an athlete gets a running start and tries to leap as far as...
Vector Mechanics For Engineers
Find the change in length of side AB.
Mechanics of Materials, 7th Edition
Locate the centroid of the area. Prob. 9-17
INTERNATIONAL EDITION---Engineering Mechanics: Statics, 14th edition (SI unit)
A biological fluid moves at a flow rate of m=0.02kg/s through a coiled, thin-walled, 5-mm-diameter tube submerg...
Fundamentals of Heat and Mass Transfer
What types of polymers are most commonly blow molded?
DeGarmo's Materials and Processes in Manufacturing
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- 6. The following engineering stress-strain data were obtained for 0.2% C plain carbon steel. (a) Plot the engineering stress-strain curve (b) Determine the ultimate tensile strength for the alloy (c) Determine the percent elongation at fracture (d) Plot the true stress-strain curve Engineering strain, in./in. Engineering stress, ksi 30 0.001 55 0.002 60 0.005 68 0.01 72 0.02 74 0.04 75 0.06 76 0.08 75 0.1 73 0.12 69 0.14 65 0.16 56 0.18 51 0.19(fracture)arrow_forwardForce P and length change AL data are given in table below for the initial portion of a tension test on 7075-T651 Al alloy. The diameter before testing was 9.07 mm., and the gage length Linitial for t length change measurement was 50.8 mm. What tension force is required to cause yielding in a bar of the same material but with a diameter of 20 mm? P, kN AL mm 7.22 0.0839 14.34 0.1636 21.06 26.8 31.7 34.1 35.0 0.241 0.308 0.380 0.484 0.614 36.0 0.924 36.5 1.279 36.9 37.2 1.622 1.994arrow_forwardA 1045 hot-rolled steel tension test specimen has the original diameter and length of 6 mm and 25 mm, respectively. The load and change in length data were recorded as shown in Table 1 below: Table 1. Load and change in length Load (KN) Change in Length Load (KN) Change in Length (mm) (mm) 20.56 2.26 2.94 0.01 20.72 3.36 5.58 0.02 20.61 3.83 8.52 0.03 19.97 4.00 11.16 0.04 18.72 Fracture. 12.63 0.05 13.02 0.06 13.16 0.08 13.22 0.10 16.15 0.61 18.50 1.04 20.27 1.80 Page 16 3.1) Calculate stress and strain for the data in Table 1. Please show 1 calculation of stress and 1 of strain. The rest you must tabulate.arrow_forward
- 8. A cylindrical bar of steel with a diameter of 10 mm is deformed elastically by applying a force along the bar axis. Determine the force that produces an elastic reduction in diameter of 3 X 10-³ mm. You may use material properties given in Table 6.1 below. Table 6.1 Room-Temperature Elastic and Shear Moduli and Poisson's Ratio for Various Metal Alloys Metal Alloy Aluminum Brass Copper Magnesium Nickel Steel Titanium Tungsten GPa 69 97 110 45 207 207 107 407 Modulus of Elasticity 10 psi 10 14 16 6.5 30 30 15.5 59 Shear Modulus GPa 25 37 46 17 76 83 45 160 10° psi 3.6 5.4 6.7 2.5 11.0 12.0 6.5 23.2 Poisson's Ratio 0.33 0.34 0.34 0.29 0.31 0.30 0.34 0.28arrow_forwardAn S-N plot from fatigue testing of a steel is provided below. Use the plot to determine the following values for this steel. 1. Fatigue limit: 2. Fatigue lifetime at a stress amplitude of: 415 MPa: 275 MPa: 3. Fatigue strength at: 5x104 cycles: 5x105 cycles 500 400 300 200 100 0 1.E+04 Stress Amplitude (MPa) 1.E+05 1.E+06 Cycles to Failure 1.E+07 1.E+08arrow_forward3. A cylindrical specimen of cold-worked copper has a ductility, %EL. If its cold-worked radius is d, what was its radius before deformation? Use %EL=25%; d = 10mm Ductility (%EL) 70 60 50 40 30 20 Brass 1040 Steel 10 Copper 0 0 10 110 20 30 40 50 60 70 Percent cold workarrow_forward
- Force P and length change AL data are given in table below for the initial portion of a tension test on 7075-T651 Al alloy. The diameter before testing was 9.07 mm., and the gage length Linitial for t length change measurement was 50.8 mm. Determine the yield strength with offset limit, and %total elongation. P, kN AL mm 7.22 14.34 0.0839 0.1636 21.06 0.241 26.8 0.308 31.7 0.380 34.1 0.484 35.0 0.614 36.0 0.924 36.5 1.279 36.9 1.622 37.2 1.994arrow_forward5. The following data were collected from a standard 0.505-in.-diameter test specimen of a copper alloy (initial length lo= 2.0 in.). After fracture, the total length was 3.014 in. and the diameter was 0.374 in. Load (Ib) Al (in.) 00000 3,000 6,000 0.00167 0.00333 7,500 0.00417 9,000 10,500 0.0090 0.040 12,000 0.26 12,400 11,400 0.50 (maximum load) 1.02 (fracture) a) Plot the data as engineering stress versus engineering strain. b) Compute the modulus of elasticity. c) Determine the yield strength at a strain offset of 0.002. d) Determine the tensile strength of this alloy. e) What is the approximate ductility, in percent elongation? f) Compute the modulus of resilience. g) Compute from the data and plot true stress versus true strain diagram.arrow_forwardThe engineering stress-strain curve below was obtained for a precipitation hardened Aluminum alloy. What is the approximate Yield Strength for this alloy in psi? Engineering Stress Based on Original Area (psi) 50,000 45,000 40,000 35,000 30,000 25,000 20,000 15,000 10,000 5,000 0 O 0.02 0.04 0.06 Aluminum 6061-T6 0.08 0.1 0.12 Engineering Strain (in/in) 0.14 X 0.16 0.18arrow_forward
- The stress-strain data from a tensile test on a cast-iron specimen are € (10-3) 0 0.20 0.44 0.80 1.0 1.5 2.0 26 32 40 46 49 54 NOTE: This is a multi-part question. Once an answer is submitted, you will be unable to return to this part. 2.8 3.4 4.0 5.0 a (kpsi) 0 5 10 16 19 Determine the tangent modulus, E, at a value of a=0 psi. 106 psl. The tangent modulus, Eis Xarrow_forward140 900 1040 Steel Percent cold work = 0 %3D 120 Yield strength = 200 MPa 800 Yield strength = 29 ksi 700 100 600 Brass -80 500 400 60 Copper 300 40 200 10 20 40 30 50 60 70 Percent cold work Tensile strength (MPa) Tensile strength (ksi)arrow_forwardA study investigated the effects of cyclic loading and environmental conditions on fatigue crack growth at a constant 22 MPa stress for a particular material. The data from this experiment are shown below (the response is crack growth rate). Frequency Environment Air H2O Salt H2O 10 2.29 2.06 1.90 2.47 2.05 1.93 2.48 2.23 1.75 2.12 2.03 2.06 1 2.65 3.20 3.10 2.68 3.18 3.24 2.06 3.96 3.98 2.38 3.64 3.24 0.1 2.24 11.00 9.96 2.71 11.00 10.01 2.81 9.06 9.36 2.08 11.30 10.40 Analyze the data from this experiment (use α = 0.05). Show the ANOVA table. Analyze the residuals. Show the residual plots. Repeat the analyses from parts (a) and (b) using ln(y) - natural log as the response. Comment on the results.arrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University Press
Mechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSON
Thermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEY
Mechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage Learning
Engineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Material Properties 101; Author: Real Engineering;https://www.youtube.com/watch?v=BHZALtqAjeM;License: Standard YouTube License, CC-BY