Applied Statics and Strength of Materials (6th Edition)
6th Edition
ISBN: 9780133840544
Author: George F. Limbrunner, Craig D'Allaird, Leonard Spiegel
Publisher: PEARSON
expand_more
expand_more
format_list_bulleted
Textbook Question
Chapter 10, Problem 10.4P
The data from the tension test of a steel specimen are given in Table 10.2. The gage length was 2.000 in, and the original diameter was 0.505 in. The final diameter was 0.397 in. Calculate stress and strain at each point and draw the stress-strain diagram. Estimate the value of the modulus of elasticity, upper and lower yield points, ultimate strength, rupture strength, and percent reduction in area. (Hint: Draw a second curve exaggerating the strain scale for the first eight points. See Figure 10.3. )
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
The data shown in the table below were obtained from a tensile test of high-strength steel. The test specimen had a diameter of 13mm and a gage length of 50mm. At fracture, the elongation between the gage marks was 3.0mm and the minimum diameter was 10.7mm.
Plot the conventional stress-strain curve for the steel and determine the propotional limit, modulus of elasticity (i.e the slope of the initial part of the stress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 50mm, and percent reduction area.
TENSILE-TEST DATA
Load(kN)
Elongation(mm)
5
0.005
10
0.015
30
0.048
50
0.084
60
0.099
64.5
0.109
67.0
0.119
68.0
0.137
69.0
0.160
70.0
0.229
72.0
0.259
76.0
0.330
84.0
0.584
92.0
0.853
100.0
1.288
112.0
2.814
113.0
Fracture
The following stress-strain curve was prepared based on a tensile test of a specimen that had a circular cross-section. The gage
diameter of the specimen was 0.25 inches and the gage length was 4 inches. The stress scale of the stress-strain diagram is
given with the factor a = 10 ksi. Estimate:
(a) The modulus of elasticity.
(b) The ultimate strength.
(c) The yield strength (0.2% offset).
(d) The percent elongation at fracture.
2013 Michael Swanbom
STRESS VS. STRAIN
BY NC SA
7a
bat
Sat
2at
at
0.05
STRAIN
0.01
0.04
0.06
0.08
0.02
0.03
0.07
0.09
STRESS
The Highest load sustained druing an uniaxial
tensile testing experiment is 7,500lb. If the original
cross section has a diamter of 0.25in, what is the
ultimate tensile strength? (please also make a
drawing)
Chapter 10 Solutions
Applied Statics and Strength of Materials (6th Edition)
Ch. 10 - A 916 - in. - diameter steel rod is tested in...Ch. 10 - A concrete cylinder 150 mm in diameter was tested...Ch. 10 - Prob. 10.3PCh. 10 - The data from the tension test of a steel specimen...Ch. 10 - An 18-in.-long titanium alloy rod is subjected to...Ch. 10 - ASTM A36 steel rods are used to support a balcony....Ch. 10 - A 450-mm-long AISI 1020 steel rod is subjected to...Ch. 10 - A tension member in a roof truss is composed of...Ch. 10 - A short, solid, compression member of circular...Ch. 10 - A main cable in a large bridge is designed for a...
Ch. 10 - Test results of a steel specimen indicated an...Ch. 10 - A concrete canoe in storage is supported by two...Ch. 10 - A load is applied to a rigid bar that is...Ch. 10 - Prob. 10.14CPCh. 10 - Write a program that will allow a user to input...Ch. 10 - A 12 - in. - diaiíct.cr structural nickel steel...Ch. 10 - Compute the modulus of elasticity of a copper...Ch. 10 - A concrete cylinder 6 in. in diameter was tested...Ch. 10 - An aluminum bar 2 in. by 12 - in. in cross section...Ch. 10 - During a tensile test of a steel specimen, the...Ch. 10 - A 12.5-mm-diameter steel rod was subjected to a...Ch. 10 - Prob. 10.22SPCh. 10 - A standard steel specimen having a diameter of...Ch. 10 - 10.24 A tension member in a structure is composed...Ch. 10 - A pair of wire cutters is designed to operate...Ch. 10 - Calculate the end bearing length required for a...Ch. 10 - Design a 3-m-long rod subjected to a tensile load...Ch. 10 - The collar bearing shown is subjected to a...Ch. 10 - A 10-ft-long steel member is subjected to a...Ch. 10 - Two steel bars A and B support a load P, as shown....Ch. 10 - Prob. 10.31SP
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.Similar questions
- . From the tensile stress-strain behaviour for a casted iron as shown in the following curve. Please answer the following questions (1) Estimate the modulus of elasticity, (2) Calculate the change in length of a specimen with original length of 100mm that is subjected to a tensile stress of 300MPa. (Hint: Using the Hooke's law to get the strain.) 600 500 400 - 300 - 200 - 100 - 2 4 6. 8 10 12 14 16 Strain Strength (MPa)arrow_forwardA stress-strain diagram for a tension test of an alloy steel sample is shown in the diagram below. The initial sample diameter is 0.502”, the diameter of the fractured sample is 0.412”, the original gage length is 2.00” and the final length after fracture is 2.78”. Determine/ calculate the following: (a) The stress at the proportional limit. (b) The modulus of elasticity (E). (c) The yield stress using the 0.2% offset method. (d) Theultimatetensilestrength. (e) The rupture stress. (f) The percent reduction in area. (g) The percent elongation. (h) Is the material considered ductile or brittle?arrow_forwardThe data shown in the accompanying table are From a tensile test of high-strength steel. The test specimen has a diameter of 0.505 in. and a gage length of 2.00 in. (see figure for Prob. 1.5-3). At fracture, the elongation between the gage marks is 0.12 in. and the minimum diameter is 0.42 in. Plot the conventional stress-strain curve for the steel and determine the proportional limit, modulus of elasticity (the slope of the initial part of thestress-strain curve), yield stress at 0.1% offset, ultimate stress, percent elongation in 2.00 in., and percent reduction in area. TENSILE-TEST DATA FOR PROB. L.5-7 Laid (lb) Elongation (in) 1000 0.0002 2000 0.0006 6000 0.0019 10,000 0.0033 12,000 0.0039 12,900 0.0041 13,400 0.0047 13,600 0.0054 13,800 0.0063 14,000 0.0090 14,400 0.0102 15,200 0.0130 16,800 0.0230 18,400 0.0336 20,000 0.0507 22,400 0.1108 22,600 Fracturearrow_forward
- Problems 2. Mild Steel is tested in the laboratory. The data obtained are: Length of Specimen = 320 mm / Diameter of Specimen = 30 mm / Elongation under a load of 20 kN = 0.055 mm Load at Yield Point = 130 kN Maximum Load = 210 kN Load at fracture = 115 kN Length of Specimen at failure = 380 mm Diameter of Specimen at failure = 17.5 mm Calculate (1).Young's Modulus (2). Yield Stress (3). Ultimate Stress (4). Fracture Stress (5). % Elongation (6). % Reduction in Area.arrow_forwardA pine wood specimen was prepared with actual dimensions of 50 mm *50 mm * 250 mm and grain parallel to its length. The deformation was measured over a gauge length of 200 mm. The specimen was subjected to compression parallel to the grain to failure. The load–deformation results are as shown in Table P10.25. a. Using a computer spreadsheet program, plot the stress–strainrelationship.b. Calculate the modulus of elasticity.c. What is the failure stress?arrow_forwardA sample test rod made of a ferrous material of 0.5 in. diameter was tested for tensile strength with the gauge length of 2.5 in. The following observations were recorded: Final length = 3.15 in; Final diameter = 0.275 in; Yield load = 7650 lb. and Ultimate load = 10375 lb. (a) Calculate: 1. yield stress, 2. ultimate tensile stress, 3. percentage reduction in area, and 4. percentage elongation. (b) What specific material, if any, is similar to this tested rod? Refer to AT7 and AT8. (c) This same material is then used as a tension member 55 inches long and is subjected to a maximum load of 6000 lb, repeated but not reversed. (d) Solve part (c) if the total elongation is not to exceed 0.025 in.? 1. %3Darrow_forward
- 1. A cylindrical steel specimen, with an initial diameter of 7mm, has elongated by 40% at the point when it starts to neck down. The load at the start of necking is 35 kN. What is the true stress at the ultimate tensile stress? The answer is 1273, but I'm not getting that. Please answer soon and neatly. Don't copy or I will dislike u many.arrow_forward2. A metal alloy has been tested in a tensile test with the following results for the flow curve parameters: strength coefficient = 620.5 MPa and strain-hardening exponent 0.26. The same metal is now tested in a compression test in which the starting height of the specimen = 62.5 mm and its diameter = 25 mm. Assuming that the cross section increases uniformly, determine the load required to compress the specimen to a height of (a) 50 mm and (b) 37.5 mm. 3. The starting length of a shaft is 25.00 mm. This shaft is to be inserted into a hole in an expansion fit assembly operation. To be readily inserted, the shaft must be reduced in length by cooling. Determine the temperature to which the shaft must be reduced from room temperature (20° C) in order to reduce its length to 24.98 mm. Refer to the Table below. Volumetric properties in U.S. customary units for selected engineering materials. Coefficient of Thermal Expansion, a Density, p Ib/in Melting Point, T Material g/cm C'x 10 F'x 10 6…arrow_forwardA 3-mm-long gold alloy wire intended to electricallybond a computer chip to its package has an initial diameter of30 μm. During testing, it is pulled axially with a load of 15grams-force. If the wire diameter decreases uniformly to29 μm, compute the following:a. The final length of the wire.b. The true stress and true strain at this load.c. The engineering stress and strain at this load.arrow_forward
- A brass specimen is subjected to a Tensile test in a laboratory. The following data obtained are: Length of Specimen = 322 mm; Diameter of Specimen = 10 mm; Yield Stress = 1279 MPa; Ultimate Stress = 2446 N/mm²; Fracture Stress = 1780 MPa; % of Elongation = 49 % % of Reduction in area = 27 %. Determine the elongation at 43 kN, Load at yielding, Maximum load, Load at fracture, Final Length & Final diameter. Take Young's Modulus as 118 GPa.arrow_forwardA square specimen of is loaded using a three-point bend test. The load during the test is 419.6 N while the separation between the load points is 53.1mm. The flexural strength of MgO is equal to 103.4MPa . Compute the minimum possible thickness the specimen should have to avoid fractures during the bend test. Round your answer to three significant figures.arrow_forwardtensile test uses a circular test specimen that has a gage length of 50 mm and diameter = 20 mm. During the test the specimen yields under a load of 100,000 N. The corresponding gage length = 50.5 mm. This is the 0.2% yield point. The maximum load of 180,000 N is reached at a gage length = 65 mm. Determine (a) yield strength, (b) modulus of elasticity, and (c) tensile strength. (d) If fracture occurs at a gage length of 73 mm, determine the ductility. i need clear ans by hand and solve very very fast in 20 min and thank you | DYBALAarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY
Elements Of Electromagnetics
Mechanical Engineering
ISBN:9780190698614
Author:Sadiku, Matthew N. O.
Publisher:Oxford University Press
Mechanics of Materials (10th Edition)
Mechanical Engineering
ISBN:9780134319650
Author:Russell C. Hibbeler
Publisher:PEARSON
Thermodynamics: An Engineering Approach
Mechanical Engineering
ISBN:9781259822674
Author:Yunus A. Cengel Dr., Michael A. Boles
Publisher:McGraw-Hill Education
Control Systems Engineering
Mechanical Engineering
ISBN:9781118170519
Author:Norman S. Nise
Publisher:WILEY
Mechanics of Materials (MindTap Course List)
Mechanical Engineering
ISBN:9781337093347
Author:Barry J. Goodno, James M. Gere
Publisher:Cengage Learning
Engineering Mechanics: Statics
Mechanical Engineering
ISBN:9781118807330
Author:James L. Meriam, L. G. Kraige, J. N. Bolton
Publisher:WILEY
Understanding Failure Theories (Tresca, von Mises etc...); Author: The Efficient Engineer;https://www.youtube.com/watch?v=xkbQnBAOFEg;License: Standard youtube license