Textbook Question
Chapter 1, Problem 1.12QP
The rectangular metal block shown in Figure P1.11 is subjected to tension within the elastic range. The increase in the length of a is 0.05 mm and the Poisson’s ratio for the material is 0.33. If the original lengths of a and b were 50 mm and 25 mm, respectively, what is the change in the length of b? Is this change expansion or contraction?
Expert Solution & Answer
Want to see the full answer?
Check out a sample textbook solutionStudents have asked these similar questions
A round steel alloy bar with a diameter of 19 mm and a gauge length of 76 mm
was subjected to tension, with the results shown in Table P3.26. Using a
computer spreadsheet program, plot the stress-strain relationship. From the
graph, determine the Young's modulus of the steel alloy and the deformation
corresponding to a 37 kN load.
TABLE P3.26
Deformation,
Load, kN
mm
9
0.0286
18
0.0572
27
0.0859
36
0.1145
45
0.1431
54
0.1718
Figure P1.16 shows the stress–strain relations of metals A and B during tension tests until fracture. Determine the following for the two metals (show all calculations and units):
Proportional limit
Yield stress at an offset strain of 0.002 in./in.
Ultimate strength
Modulus of resilience
Toughness
Which metal is more ductile? Why?
A specimen of steel has a rectangular cross section 20 mm wide and 40 mm thick, an elastic modulus of 207 GPa, and a Poisson's ratio
of 0.30. If this specimen is pulled in tension with a force of 60,000 N, what is the change in width if deformation is totally elastic?
O Increase in width of 3.62 x 10-6 m
O Decrease in width of 7.24 x 10-6 m
Increase in width of 7.24 x 106 m
O Decrease in width of 2.18 x 10-6 m
Chapter 1 Solutions
Materials for Civil and Construction Engineers (4th Edition)
Ch. 1 - State three examples of a static load application...Ch. 1 - A material has the stressstrain behavior shown in...Ch. 1 - A tensile load of 50.000 lb is applied to a metal...Ch. 1 - A tensile load of 190 kN is applied to a round...Ch. 1 - A cylinder with a 6.0 in. diameter and 12.0 in....Ch. 1 - A metal rod with 0.5 inch diameter is subjected to...Ch. 1 - A rectangular block of aluminum 30 mm 60 mm 90...Ch. 1 - A plastic cube with a 4 in. 4 in. 4 in. is...Ch. 1 - A material has a stressstrain relationship that...Ch. 1 - On a graph, show the stressstrain relationship...
Ch. 1 - The rectangular block shown in Figure P1.11 is...Ch. 1 - The rectangular metal block shown in Figure P1.11...Ch. 1 - A cylindrical rod with a length of 380 mm and a...Ch. 1 - A cylindrical rod with a radius of 0.3 in. and a...Ch. 1 - A cylindrical rod with a diameter of 15.24 mm and...Ch. 1 - The stressstrain relationship shown in Figure...Ch. 1 - A tension test performed on a metal specimen to...Ch. 1 - An alloy has a yield strength of 41 ksi, a tensile...Ch. 1 - Prob. 1.21QPCh. 1 - Figure P1.22 shows (i) elasticperfectly plastic...Ch. 1 - An elastoplastic material with strain hardening...Ch. 1 - A brace alloy rod having a cross sectional area of...Ch. 1 - A brass alloy rod having a cross sectional area of...Ch. 1 - A copper rod with a diameter of 19 mm, modulus of...Ch. 1 - A copper rod with a diameter of 0.5 in., modulus...Ch. 1 - Define the following material behavior and provide...Ch. 1 - An asphalt concrete cylindrical specimen with a...Ch. 1 - What are the differences between modulus of...Ch. 1 - Prob. 1.33QPCh. 1 - A metal rod having a diameter of 10 mm is...Ch. 1 - What is the factor of safety? On what basis is its...Ch. 1 - Prob. 1.36QPCh. 1 - Prob. 1.37QPCh. 1 - A steel rod, which is free to move, has a length...Ch. 1 - In Problem 1.38, if the rod is snugly fitted...Ch. 1 - A 4-m-long steel plate with a rectangular cross...Ch. 1 - Estimate the tensile strength required to prevent...Ch. 1 - Prob. 1.42QPCh. 1 - Briefly discuss the variability of construction...Ch. 1 - In order to evaluate the properties of a material,...Ch. 1 - A contractor claims that the mean compressive...Ch. 1 - A contractor claims that the mean compressive...Ch. 1 - Prob. 1.47QPCh. 1 - Prob. 1.48QPCh. 1 - Prob. 1.49QPCh. 1 - Briefly discuss the concept behind each of the...Ch. 1 - Referring to the dial gauge shown in Figure P1.51,...Ch. 1 - Repeat Problem 1.51 using the dial gauge shown in...Ch. 1 - Measurements should be reported to the nearest...Ch. 1 - During calibration of an LVDT, the data shown in...Ch. 1 - During calibration of an LVDT, the data shown in...
Knowledge Booster
Learn more about
Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, civil-engineering and related others by exploring similar questions and additional content below.Similar questions
- S Figure P1.16 shows the stress-strain relations of metals A and B during ten- sion tests until fracture. Determine the following for the two metals (show all calculations and units): a. Proportional limit b. Yield stress at an offset strain of 0.002 m/m. c. Ultimate strength d. Modulus of resilience e. Toughness f. Which metal is more ductile? Why? 900 Metal A 600 Metal B 300 0.00 0.02 0.04 0.06 0.08 0.10 0.12 0.14 Strain, m/m FIGURE P1.16 Stress, MPaarrow_forwardA tension test performed on a metal specimen to fracture produced the stress– strain relationship shown in Figure P1.14. Graphically determine the following (show units and all work): a. Modulus of elasticity within the linear portion. b. Yield stress at an offset strain of 0.002 m/m. c. Yield stress at an extension strain of 0.005 m/m. d. Secant modulus at a stress of 525 MPa. e. Tangent modulus at a stress of 525 MPa.arrow_forwardPROBLEM 4: As shown in the diagram shown, there is a gap of 0.5 mm between the rods at 10°C. Determine the stress in each rod if the temperature is raised to 150°C. The properties of each material are shown in the diagram. 0.5 mm FINAL ANSWERS 300 mm -250 mm MPa O alum O steel MPа Aluminum Stainless steel A = 2000 mm2 E = 75 GPa a = 23 × 10-6°C A = 800 mm? E = 190 GPa 17.3 x 10-6/°Carrow_forward
- 2. A steel bar, whose cross section is 0.55 inch by 4.05 inches, was tested in tension. An axial load of P = 30,500 lb. produced a deformation of 0.105 inch over a gauge length of 2.05 inches and a decrease of 0.0075 inch in the 0.55-inch thickness of the bar. Determine the lateral strain. * Your answer Determine the axial strain. Your answer Determine the Poisson's ratio v. * Your answer Determine the decrease in the 4.05-in. cross-sectional dimension (in inches). * Your answerarrow_forwardA piece of 50 mm x 30 mm material experiences a homogenous deformation as shown in the figure below. The deformed shape in x-y plane is illustrated by the solid lines. If E = 3.9 GPa and the Poisson's Ratio is 0.35, what is the associated shear stress? provide your answer in MPa with precision to two decimal points. Answer: 0.014 30 0.010 y 0.009 0.012 50arrow_forwardA tension test performed on a metal specimen to fracture produced the stress- strain relationship shown in Figure P1.14. Graphically determine the following (show units and all work): a. Modulus of elasticity within the linear portion. b. Yield stress at an offset strain of 0.002 in./in. c. Yield stress at an extension strain of 0.005 in/in. d. Secant modulus at a stress of 525MPA.arrow_forward
- 1.17 Figure P1.17 shows the stress-strain relations of metals A and B during tension tests until fracture. Determine the following for the two metals (show all calcu- lations and units): a. Proportional limit b. Yield stress at an offset strain of 0.002 in./in. 150 - - Metal A 100 • Metal B 50 0.00 0.02 0.04 0.06 0.08 0.10 0.12 0.14 Strain, in./in. FIGURE P1.17 c. Ultimate strength d. Modulus of resilience e. Toughness f. Which metal is more ductile? Why? Stress, ksiarrow_forwardThe tension of a specimen of steel having an initial diameter of 0.507 in. was tested using a gauge length of 2 in. The following data were obtained for the elastic and plastic states. For the elastic state PAlb) 10 1000 2000 3000 4000 7000 8400 8800 9200 For the plastic state PAlb) 8800 9200 9100 13200 15200 17000 16400 14800 A/(in) 10 The reduction in the area Ris 0.0004 0.0006 0.0010 0.0013 0.0023 0.0028 0.0036 0.0089 NOTE: This is a multi-part question. Once an answer is submitted, you will be unable to return to this part. % A, (in2) 0.1984 0.1978 0.1963 0.1924 0.1875 0.1563 0.1307 0.1077 What are the values of the yield strength, Sy and the reduction in the area? The value of the yield strength Sy is [ kpsl. 4arrow_forward2. Given that a steel cylinder of dimenslons 12.0 mm in dlameter and 70 mm long is subjected to tensicn. (a) Determine the modulus of elasticity in the figure below. (b) Using the figure below, calculate the deformation in the steel cylinder subjected to 15 kN tension for ce. 600 500 400 500 400E 300 300 200 200 100 100 0.000 0.002 0.004 0.006 Strain 8.00 0.04 0.03 0.12 0.16 0.20 Strain Tensile stress-strain behavior for a steel alloy. Daccri be io v our MP MOrds the throo ctrongthanin g arnin cize rad uction colid Stress (MPa) Stress (MPa)arrow_forward
- A steel bar 100 mm long is subjected to a tensile stress o. If change in length of bar is 0.05 mm what is the value of o? Given E = 200 GPaarrow_forwardA piece of (A= 27 mm,B= 43 mm) material experiences a homogenous deformation. The deformed shape in x-y plane is illustrated by the solid lines. What is the value of the shear strain? provide your answer in six decimal points. 0.01 0.02 Answer: A B 0.015arrow_forwardA steel alloy specimen having a rectangular cross section of dimensions 19.1 mm x 3.1 mm (0.7520 in. × 0.1220 in.) has the stress-strain behavior shown in the Animated Figure 6.22b. If this specimen is subjected to a tensile force of 98290 N (22100 Ib;) then (a) Determine the amount of elastic strain induced. (b) Determine the amount of plastic strain induced. (c) If its original length is 610 mm, what will be its final length after this force is applied and then released? The elastic modulus for steel is 207 GPa. (a) i (b) i (c) i mmarrow_forward
arrow_back_ios
SEE MORE QUESTIONS
arrow_forward_ios
Recommended textbooks for you
- Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning
Materials Science And Engineering Properties
Civil Engineering
ISBN:9781111988609
Author:Charles Gilmore
Publisher:Cengage Learning
Material Properties 101; Author: Real Engineering;https://www.youtube.com/watch?v=BHZALtqAjeM;License: Standard YouTube License, CC-BY