A tensile force of 20 kN is applied to a specimen with a gage length of 50mm. It is then noted that the distance between the gage marks became 50.122mm. a,) What is the modulus of elasticity of the specimen if its diameter is 10mm? b.) What is the axial stress of the specimen? Solution must have Free Body Diagram/drawing.

A tensile force of 20 kN is applied to a specimen with a gage length of 50mm. It is then noted that the distance between the gage marks became 50.122mm. a,) What is the modulus of elasticity of the specimen if its diameter is 10mm? b.) What is the axial stress of the specimen? Solution must have Free Body Diagram/drawing.

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.3P: A tensile test was performed on a metal specimen having a circular cross section with a diameter 0....

See similar textbooks

Similar questions

The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.
The results of a tensile test are shown in Table 1.5.2. The test was performed on a metal specimen with a circular cross section. The diameter was 3 8 inch and the gage length (The length over which the elongation is measured) was 2 inches. a. Use the data in Table 1.5.2 to produce a table of stress and strain values. b. Plot the stress-strain data and draw a best-fit curve. c. Compute the, modulus of elasticity from the initial slope of the curve. d. Estimate the yield stress.
PROBLEMS 203. During a stress-strain test, the unit deformation at a stress of 5000 psi Wap ODserved to be 0.000167 in./in. and at a stress of 20,000 psi it was 0.000667 in./in. If the proportional limit is 30,000 psi, what is the modulus of elasticity? What is the stress corresponding to a strain of 0.0002 in./in.? Would these re- sults be valid if the proportional limit were 18,000 psi? Explain. E = 30 X 106 psi; S 6000 psi %3D Ans. 204. A uniform bar of length L, cross-sectional area A, and weight W is sus- WL If pended vertically from one end. Show that its total elongation is & = 2AE wL? its weight per unit volume is w, show also that & 2E A steel rod having a cross-sectional area of sq in. and a length of 600 ft is suspended vertically. It supports a load of 5000 lb at the lower end. If steel 30 X 106 psi, find the total elongation in the rod. Ans. 8 = 2.64 in. 205 weighs 490 lb/cu ft and E Hint: Use the result of Prob. 204. steel wire 30 ft long, hanging vertically, supports a…
Determine stress value
y 400 mm 4 mm B 200 mm A 6 mm The rectangular plate is subjected to the deformation shown by the dashed line. Determine the average shear stress in the plate if the shear modulus of the material is 2 MPa. Express your answer in kPa and round it to the nearest integer if necessary.
A)Define poison's ratio B)A tensile-test piece of diameter 10mm is subjected to an axial force of 15KN.If E for the material is 207KN/mm^2 and poison's ratio is 0.29, calculate the lateral strain and the change in diameter.
At the proportional limit, the axial load of a 0.70-in-diameter bar was 5400 lb. A 2.20-in. gauge length on the bar has increased by 0.0040 inch. a) Determine the strain in the bar.b) Determine the elastic modulus (in ksi)
4. Sample of steel bar has 50 mm length after performing tension test the final length was 50.2 mm, strain of this sample equal to * 0.04% 0.4% 4% 0.004% O All above are not correct
Define the term neutral stress.
In a standard tensile test, an aluminum rod of 20-mm diameter is subjected to a tension force of P- 30 kN. Knowing that E- 70 GPa, and the change in diameter of the rod- 0.00955 mm, determine the poissons' ratio v. 20n diateter gage length-150 0.33 O 0.6 0.29 O 0.35
A metal specimen with 20 mm diameter and 100 mm gauge length is loadedelastically with 5 kN and elongates 0.8 mm. Its diameter under this load is 19.95 mm. Calculate:a) the Bulk Modulus, Kb) the Shear Modulus, G
What is unconfined compressive strength test, which triaxial compression test is similar to shows? If the maximum compressive stress value obtained from this test is qu, this test Show the shear strength of the specimen using the Mohr tensile circle. Also, short Why is the unconfined compressive strength of the Comment on its use. I will understand better if you type the answers with the keyboard thank you.