3. A strip of chicken skin was excised for mechanical testing in tension. The initial dimension of the rectangular specimen was 30 mm long and 15 mm wide, with average thickness of 3 mm. The mechanical testing was conducted at a rate of 5 mm/sec. The following data were obtained: gauge length, mm 20 22 24.2 26.3 27.9 30.1 force, N 0 0.8 2.7 7.9 12.9 19.6 a. Calculate the engineering stresses and strain from the information given and plot the stress-strain curve. Assume that 5 mm of the specimen length is clamped by the testing grip at each end, such that the initial gauge length of the specimen is 20 mm.

3. A strip of chicken skin was excised for mechanical testing in tension. The initial dimension of the rectangular specimen was 30 mm long and 15 mm wide, with average thickness of 3 mm. The mechanical testing was conducted at a rate of 5 mm/sec. The following data were obtained: gauge length, mm 20 22 24.2 26.3 27.9 30.1 force, N 0 0.8 2.7 7.9 12.9 19.6 a. Calculate the engineering stresses and strain from the information given and plot the stress-strain curve. Assume that 5 mm of the specimen length is clamped by the testing grip at each end, such that the initial gauge length of the specimen is 20 mm.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

I want answers to all four questions if possible. Thanks for help :) Following experimental data are obtained from tensile test of a rectangular test specimen with original thickness of 2,5 mm, gauge width of 24 mm and gauge length of 101 mm: Load (N) Elongation (mm) 0 0 24372 0,183 23008 0,315 28357 5,777 35517 12,315 27555 17,978 23750 23,865 Based on the information above; draw stress-strain diagram of the material and answer the following questions. - Calculate the fracture strength (in MPa) of the material. - Calculate the percent elongation of the specimen at fracture point. - Determine the modulus of resilience (in N.mm/mm3) of the material. (Use at least five decimal units) - Determine the toughness index number (in N.mm/mm3) of the material.
The following data were collected from a 12 mm diameter test specimen of Magnesium. LOAD (N) 0 5000 10000 15000 20000 25000 26500 27000 26500 25000 GAUEGE LENGTH (mm) 30.000 30.0296 30.0592 30.0888 30.15 30.51 30.90 31.50 (maximum load) 32.10 32.79 (fracture) After the fracture, the gauge length is 32.61 mm and the diameter is 11.74 mm. a) What is the elastic modulus? b) Percent elongation at fracture? c) Percent elongation after fracture? d) What is the Poisson's ratio? e)Draw the engineering stress-strain diagram corresponding to the values in the table. Call this plot I. Now consider this experiment is repeated at a higher temperature with an identical sample. Draw the new engineering stress-strain diagram, call it plot Il and highlight the differences (on the same graph) between I and II.
The following data were recorded during the tensile test of a test specimen with a diameter of 12.8 mm. The gage length is 50.8 mm. The given data are as follow; Given: Test specimen material: Aluminum Diameter of test specimen: Do = 12.8 mm Length of test specimen: Lo = 50.8 mm Force and Elongation data for test specimen Assumptions: 1. The given data is accurate and the material is isotropic 2. The direction of applied force is parallel to the length of the cylinder Requirement: To interpret and plot the stress Vs Strain curve for a given specimen DATA: LENGTH, mm STRESS, MPa LOAD, N 0 50.8 7 330 50.851 15 100 50.902 23 100 50.952 30 400 51.003 34 400 51.054 38 400 51.308 41 300 51.816 44 800 52.832 46 200 53.848 47 300 54.864 47 500 55.88 36 100 56.896 44 800 57.658 42 600 58.42 36 400 59.182 STRAIN
A tension test was performed on a specimen having an original diameter of 13.0 mm and a gauge length of 50 mm. Load (kN) Elongation (mm) 0 11.1 31.9 37.8 40.9 43.6 53.4 62.3 64.5 62.3 58.8 0 0.0175 0.0600 0.1020 0.1650 0.2490 1.0160 3.0480 6.3500 8.8900 11.9380 Using the data listed in the table, plot the stress-strain diagram. Use a scale of 20 mm = 50 MPa and 20 mm = 0.05 mm/mm. Part A From the diagram, determine approximately the modulus of toughness. Express your answer to three significant figures and include the appropriate units. U = Submit O μA Value Request Answer Units < Return to Assignment Provide Feedback ?
The following data were collected from a 12 mm diameter test specimen of Magnesium. LOAD (N) GAUEGE LENGTH (mm) 0 5000 10000 15000 20000 25000 26500 27000 26500 30.000 25000 30.0296 30.0592 30.0888 30.15 30.51 30.90 31.50 (maximum load) 32.10 32.79 (fracture) After the fracture, the gauge length is 32.61 mm and the diameter is 11.74 mm. a) What is the elastic modulus? b) Percent elongation at fracture? c) Percent elongation after fracture? d) What is the Poisson's ratio? e)Draw the engineering stress-strain diagram corresponding to the values in the table. Call this plot I. Now consider this experiment is repeated at a higher temperature with an identical sample. Draw the new engineering stress-strain diagram, call it plot II and highlight the differences (on the same graph) between I and II.
A tension test was performed on a specimen having an original diameter of 13.7 mm and a gauge length of 50 mm. The data are listed in the table. Load (kN) Elongation (mm) 0 11.1 31.9 37.8 40.9 43.6 53.4 62.3 64.5 62.3 58.8 0 0.0175 0.0600 0.1020 0.1650 0.2490 1.0160 3.0480 6.3500 8.8900 11.9380 Plot the stress-strain diagram. Use a scale of 20 mm = 50 MPa and 20 mm = 0.05 mm/mm. Redraw the linear-elastic region, using the same stress scale but a strain scale of 20 mm = 0.001 mm/mm. From the diagram, determine approximately the modulus of elasticity. Express your answer to three significant figures and include the appropriate units. E = Submit Part B συ = Submit Part C ☐☐ μÅ of = Value Determine the ultimate stress. Express your answer to three significant figures and include the appropriate units. Request Answer μĂ Value Request Answer Units μĂ - Value Units Determine the fracture stress. Express your answer to three significant figures and include the appropriate units. ? Units ? ?
Q1- The following data was obtained tensile test ɔn a specimen of 10 mm diameter and gauge length Lo=50 mm: 0 38 | 76.2 92.7 107 149 160.4 | 155 142 124.7 load(KN) | elongation(mm) 0 0.02 0.12 0.25 0.50 2.03 3.55 4.06 5.1 5.84 Using the graphic paper supplied, Plot engineering stress-strain curves, then determine the (ay, ey), (ou , eu), (of,, ef), modulus of elasticity, then detected in the draw ((stroin hardening (m)), (Necking), (uniform plastic region and non-uniform plastic region) and (elastic & plastic) region))?
σ (ksi) 105 90 75 60 45 30 15 0 8 0 0 0.20 0.25 0.30 0.35 0.05 0.10 0.15 0.001 0.002 0.003 0.004 0.005 0.006 0.007 € (in./in.) The stress-strain diagram from tensile test data for a metal alloy is shown. If the diameter of testing sample is 0.5 in determine: a) UTS b) Yield Strength c) Braking/ Failure Strength d) Young Module of Elasticity e) The load causing yielding in material
A tension test was performed on a specimen having an original diameter of 11.5 mm and a gauge length of 50 mm. The data are listed in the table. Load (kN) Elongation (mm) 0 11.1 31.9 37.8 40.9 43.6 53.4 62.3 64.5 62.3 58.8 0 0.0175 0.0600 0.1020 0.1650 0.2490 1.0160 3.0480 6.3500 8.8900 11.9380 Plot the stress-strain diagram. Use a scale of 20 mm = 50 MPa and 20 mm = 0.05 mm/mm. Redraw the linear-elastic region, using the same stress scale but a strain scale of 20 mm = 0.001 mm/mm. From the diagram, determine approximately the modulus of elasticity. Express your answer to three significant figures and include the appropriate units. E 215 Submit Previous Answers Request Answer Part B μÀ X Incorrect; Try Again; 2 attempts remaining Tu = 530 Determine the ultimate stress. Express your answer to three significant figures and include the appropriate units. GPa μÅ Part C Submit Previous Answers Request Answer MPa | μA ? X Incorrect; Try Again; 2 attempts remaining of=479.15 Determine the…
A tensile test was performed on a metal specimen with a diameter of 1/2 inch and a gage length (the length over which the elongation is meas- ured) of 4 inches. The data were plotted on a load-displacement graph, P vs. AL. A best-fit line was drawn through the points, and the slope of the straight-line portion was calculated to be P/AL = 1392 kips/in. What is the modulus of elasticity? BI
The following data was obtained from a tensile test on Load (kN) 16 32 56 72 95 110 132 142 140 135 Extension (mm) 0.2 0.4 0.7 0.9 1.5 2.5 5.0 8,5 10.0 12.0 a specimen of 10mm diameter and gauge length 60mm. Using the graph paper supplied, plot the load-extension diagram and determine: (1) The tensile strength (2) 0.1% Proof Stress (3) Young's Modulus for the specimen
A 50 m tape was standardized and found to be 0.0015 m longer at an observed temperature of 31.5°C under a pull of 10 kg. The same tape is used to measure a line found to be 523.61 m at an average temperature of 24.5 °C using a pull 12 kg. What is the correct length of the line?