Project 7: Decide whether you choose an amorphous or crystalline polymer for the following products and/or applications and justify your answer: A. Graphite: B. Tempered glass: C. High thermal conductivity ceramics: D. Hot coffee cups Briefly explain why amorphous polymers are transparent, while predominantly crystalline polymers appear opaque or translucent.

Project 7: Decide whether you choose an amorphous or crystalline polymer for the following products and/or applications and justify your answer: A. Graphite: B. Tempered glass: C. High thermal conductivity ceramics: D. Hot coffee cups Briefly explain why amorphous polymers are transparent, while predominantly crystalline polymers appear opaque or translucent.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Use the graph depicting specific volume versus temperature for polymers to answer the following question.: Identify the curve that exhibits both a definitive glass transition temperature and melting temperature. Group of answer choices Curve A Curve B Curve C
Draw stress-strain graphs for two polymers: one is stiffer than the other and exhibits ayield point and the other shows no clear yield point but is much tougher.
As crystallinity of polymers increases density decreases true or false
2. Plot the effect of glass temperature on phase transition (Vitrification) in amorphous polymers.
Why do crystalline polymers tend to have higher density than amorphous ones?
Describe briefly the elastic mechanism in semi-crystalline polymers 2 . Describe briefly the plastic mechanism in semi-crystalline polymers
Polyethylene Terephthalate or PET is a linear semicrystalline thermoplastic polymer widely used in food packaging. Calculate the density of this polymer when the total crystallinity is 65.4%. The density for the totally amorphous PET material is 1.33 g/cm³, and the density of the totally crystalline is 1.44 g/cm³. 1.38 g/cm³ 1.40 g/cm³ 1.42 g/cm³ 1.80 g/cm³ None of the above
Please make sure to display your thought process? It is imperative to be able to follow how the answer was deduced. Please be as thorough as possible. Please address all parts of this question as they are all part and critical to answering this question correctly. Please show good integrity when answering the question: Strain-rate, temperature, pressure, and aging time all affect the stress/strain behavior of polymers. Draw a stress-strain curve below for a typical ductile polymer. Clearly label the yield point and the ultimate tensile strength. Using this curve draw two new curves corresponding to same polymer but now tested at: 1) an increase in temperature and 2) an increase in strain rate. Explain what happens to the tensile behavior after: a) a prolong time of aging time is increased and b) when the tensile tests are conducted under super imposed hydrostatic compression
Hello. I am having trouble with one of the questions I have for my study guide for Material Science. I will list the question down below. Thanks. What are two differences between thermoplastic and thermosetting polymers?
EAC in metals causes cracks to form and grow. What other feature can form and grow in amorphous polymers suffering from EAC?
Briefly explain the shortcomings of a Maxwell mechanical model in describing the realbehaviour of polymeric materials.
The 3D printing approach shown below is fused deposition modelling (FDM), where feedstock polymer is fed into the heated printer nozzle and deposited onto the platform to form the final object in the desired geometry. Which of the polymers below are suitable for this process and what nozzle temperature should be used for that material? Z AXIS X AXIS HOME Y AXIS D LEGEND: A : Extruder B: Nozzle C: Printed part D: Hot plate E: Filament Select one or more: a. Polyvinyl chloride - 110°C (for PVC: Tg = 120°C, Tmelt = 240°C, HDT = 92 °C) b. ABS-125°C (for ABS: Tg = 140°C, Tmelt = 200°C, HDT = 100 °C) c. Polyvinyl chloride - 250°C (for PVC: Tg = 120°C, Tmelt = 240°C, HDT = 92 °C) d. ABS-215°C (for ABS: Tg = 140°C, Tmelt = 200°C, HDT = 100 °C)