In the binary phase diagram for the Cu-Ni system in the Figure provided: 1. Draw the microstructures for each point for the alloy upon cooling (A-E) and label ALL phases! 2. What are the compositions (C's) of EVERY phase and the relative phase amounts (W's) for each microstructure A-E? Show all work! T(°C) (liquid) L 20 (a, solid) 30 A BUD E 40 Co OOOOO w 10 50 wt% Ni CL= Ca= CL= Ca= CL= Ca= C₁= Cu= C₁= Ca= WL= Wa= WL= Wα= W₁= W= W₁= Wa= W₁= Wu= A B E

In the binary phase diagram for the Cu-Ni system in the Figure provided: 1. Draw the microstructures for each point for the alloy upon cooling (A-E) and label ALL phases! 2. What are the compositions (C's) of EVERY phase and the relative phase amounts (W's) for each microstructure A-E? Show all work! T(°C) (liquid) L 20 (a, solid) 30 A BUD E 40 Co OOOOO w 10 50 wt% Ni CL= Ca= CL= Ca= CL= Ca= C₁= Cu= C₁= Ca= WL= Wa= WL= Wα= W₁= W= W₁= Wa= W₁= Wu= A B E

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Calculate the weight fraction for phases at point B? what are those phases? Is there any eutectic rection? How many phases are present in this diagram? Cu-Ni system T(°C) TA 1300 -L (liquid): A tie ļine liquidus L +a Тв EB solidus (solid) 1200 TD ID 20 3032 35: 4043 50 Ca wt% Ni
For two hypotetical materials which have limitless solubility for both in the “liquid” and “solid” states in each other, the following data are listed. Melting Temperatures of material A and B are Tm,A and Tm,B respectively, Liquidus and Solidus curves are circular arcs. a- Draw the related “Phase Diagram” of Material A and Material B showing the data given and calculated. b- Calculate/Determine the compositions of phases at T2 , explain the procedure. c- Calculate/Determine the “percentages” of “phases” of Alloy,2 at T2 , explain the procedure. Given: -Tm,A, Celcius =300 -Tm,B, Celcius =800 -T1, Celcius =600 -B percentage of Liquid phase at T1 =25 -B percentage of Solid phase at T1 =70 -B percentage of Alloy 2. =50 -T2, Celcius =650 -B percentage of Liquid phase of Alloy 2 at T2 = to be calculated -B percentage of Solid phase of Alloy 2 at T2 = to be calculated
For the given Ti-Cu phase diagram, specify all temperature-composition points at which eutectics, eutectoids, peritectic, and congruent phase transformations occur. Also, for each, write the reaction upon cooling. Temperature (°C) 1700 1500 1300 1100 900 700 500 0 (Ti) 1 B a 20 Ti₂Cu 40 Composition (wt% Cu) L TiCu TigCu4 60
Temperature ("C) Temperature ($1 Consider 1 kg of Copper - Silver alloy (Cu - Ag) containing 75 wt% Ag. The phase diagram of the alloy is shown in the figure below. The alloy is cooled to 778 °C (just below the eutectic temperature). Calculate the mass in kg of the eutectic phase B (phase B that appears during the eutectic reaction) that forms? Composition (at% Ag 20 40 60 100 2200 80 1200 2000 Liquidus 1000 LIquid 1800 Solidus 1600 800 779°C (T 80 91.2 1400 IC. 1200 600 Solvus T000 400 800 200 20 40 80 100 (Cu) Composioon wt A
For 40 wt% Sn – 60 wt% Pb alloy at 150 oC (at point B) as shown in Figure, i. State the name of phase(s) present. ii. Calculate the composition(s) of the phase(s) present. 600 300 Liquid 500 a+L 200 400 300 100 200 100 20 60 100 (Pb) (Sn) Composition (wt % Sn) Temperature ("C) Temperature ("F)
b) Figure 1 shows a Cu-Ag phase diagram. Calculate the phase analysis for 50% Ag-50% Cu at 800 °C. Temperature (°C) 1200 1000 800 600 400 200 ( C (Cu) B 8.0 (C₂g) -Solidus Solvus 20 20 a + L Composition (at% Ag) 40 -Liquidus 779°C (TE) a + B 40 Liquid 60 Composition (wt% Ag) 60 71.9 (CE) 80 80 B+L 91.2 (CBg) G to 100 2200 2000 1800 F 1600 1400 1200 1000 800 600 400 100 Temperature (°F)
QI/ Draw a thermal equilibrium diagram for the binary alloy system (Si –Au), from the following data:- a- Si melts at 1414 °C, and Au melts at 1064 °C , and identify all phases are present in the diagram. b- Eutectic is formed at 360°C containing 20 Wt% Si -80 Wt% Au . c- Determine the amount of each phase for the alloy which consist 60 Wt% Si- 40Wt % Au at 1200 °C and 800 °C ,then determine the amount of eutectic at 200 °C?
1-The microstructural design of Iron-Carbon(Fe-C) alloys has led to the development of vast range of steels for structural material applications. The phase diagram provide means for producing specific microstructures. Using the phase diagram below to answer the following questions A – If the liquid mixture of Fe-3%Wt C is slowly cooled from 1600 C to 1200C indicate the phase(S) that are present at 1200 C . Also calculate the composition of the of phases.(10) B-Describe the sequence of all phase transformation that accour from Fe-1.5%wt C is slowly cooled from 1600 C to 400 C. Use the diagram below to to describe the microstructures for each phase transformation (10)
BINARY PHASE DIAGRAMS Please only answer parts d and e as the rest have been solved. Show full detailed explanation to answers with diagrams if necessary a)(i) What is the melting point of pure Mg?(ii) What is the maximum solubility of Mg in Pb and at what temperaturedoes this occur? (b) A 50 wt.% Pb-50wt% Mg alloy is slowly cooled from 700 °C to 400 °C.(i) At what temperature does the first solid phase form?(ii) What is the composition of this solid phase?(iii) At what temperature does all the liquid solidify?(iv) What is the composition of the last remaining liquid phase?(v) What is the freezing range? (c) What is the mass fraction of solid and liquid of a 60 wt.% Mg alloy at atemperature of 500 °C.(d) Draw and label the microstructure of an 80 wt.% Mg alloy at 600 °C.(e) A Mg-Pb alloy of mass 5.5 kg has a composition just slightly below thesolubility limit of 200 °C.(i) What mass of lead is in the alloy?(ii) If the alloy is heated to 350 °C how much more lead can be dissolvedin…
2. a) How many kilograms of nickel must be added to 1.75 kg of copper to yield a liquidus temperature of 1300 °C? b) How many kilograms of nickel must be added to 5.43 kg of copper to yield a solidus temperature of 1200 °C? c) The solidus and liquidus temperatures for the copper-gold system are given here. Construct the phase diagram for this system and label each region. Composition (wt.% Au) Solidus Temperature (C) Liquidus Temperature (C) 1085 1085 1019 972 20 1042 996 946 40 60 934 80 911 911 90 928 942 95 974 984 100 1064 1064
BI (a) Figure BI below shows the equilibrium phase diagram of hypothetical A - B alloy system. Answer the following questions. What are technical names of Line A and Line B? What do they signify? (i) (ii) With the aid sketches, portray the microstructures and phases that are present for the 20wt%A-80wt%B alloy (Alloy A) at the temperatures of 780 °C, 670 °C, 652 °C, and 500 °C, respectively. (iii) Assume an A - B alloy (Alloy B) has 60wt%a - 40wt%L, in terms of weight, at a temperature of 652 °C. Determine the overall composition of Alloy B. (o) emai 700 8 600 500 400 800 0 A 760 °C Line B W a /9.5 20 Line A a + L 650 °C 40 Liquid (L) wt%B Figure B1 52.5 a + ß 60 B+L 80 93.7 B 100 B
The figure below shows a hypothetical binary eutectic phase diagram on which we indicate an alloy composition of 27% B. Calculate the following quantities: a. Fraction of primary solid that forms under equilibrium cooling at eutectic temperature b. Fraction of liquid with the eutectic composition that will transform to two solid phases below the eutectic isotherm c. The amount of a and ß that will form from the liquid just below the eutectic isotherm. L+B L+a B 20 37 73 27 a +B