Given the equilibrium phase diagram (a) below, briefly describe the mechanisms of precipitation hardening/strengthening of an aluminium alloy making reference to the transitions shown in (b) below to X, X to A, X to D, A to B and A to C. a +0 B Time (a) (b) - aneaduaL Temperature

Given the equilibrium phase diagram (a) below, briefly describe the mechanisms of precipitation hardening/strengthening of an aluminium alloy making reference to the transitions shown in (b) below to X, X to A, X to D, A to B and A to C. a +0 B Time (a) (b) - aneaduaL Temperature

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Q1/ The figure below shows the phase equilibrium diagram for copper and silver Answer the following paragraphs? Conpostin a% 39 o = « & o Tepertue (F) @ Composttan (w5 ) 0 1- define pointe E? 2- define pointe B? 3- define the line AE? 4- define the line BG? 5- define the line FG?
Draw thermal equilibrium diagram for the binary alloy system (Si-Au), from the following data:- a- Silicon melts at 1414 °C, and gold melts at 1064 °C. b-Eutectic is formed at 360°C containing 20 Wt% Si -80 Wt% Au, and identify all phases are present in the diagram c-Determine the amount of each phase for the alloy which consist of 60 Wt% Si- 40Wt % Au at 1200 °C and 800 °C ,then determine the amount of eutectic at 200 °C?
A 65%Ni-35%Cu alloy is heated to be partially melted at a specific temperature T. Here, we find that Cα=70%. Estimate (1) The temperature T,(2) The liquid composition CL ,(3) The weight fractions of the solid and liquid phases.Label the corresponding condition points used.
A 10 30 70 1) For an A-B alloy of composition 25 wt% B (i) Draw the microstructure at T (just above the eutectoid temperature) and calculate the fraction of each phase in the microstructure. (ii) Draw the microstructure at T (just below the eutectoid temperature) and determine the amount of each phase, i.e., fraction of proeutectoid alpha, eutectoid alpha and eutectoid beta. 2) Provide a brief summary of phase transformations which are often observed in the iron-carbon alloy system due to various heat treatment procedures carried out to tune the microstructure. Compare mechanical strength and ductility of the materials/microstructures that form as a result of such heat treatment processes.
Phase Diagram A/ The lead and tin are partially dissolved in each other in solid state although they completely dissolved in liguid state. They form eutectic from solid solutions alfa (a) and beta (B) at alloying composition 62% tin and 38% lead, the eutectic forming temperature is 184oC. Alfa contained 20% tin dissolved in 80% lead at 1840C while beta consist of lead dissolved in tin at 1840C. If the 100 g of eutectic contained 45.5 g of alfa at 1840C. The melting temperatures of lead and tin are 3290C and 2320C respectively, and the solubility of tin and lead in each other's diminished to zero at room temperature. Plot the phase diagram for lead- tin system label all phases and temperature. Show graphically the temperature of the formation of the first solid for 42% lead alloy
Consider the binary alloy phase diagram shown schematically below. The left-hand side denotes phase a, and the right-hand side the phase ß. The intermediate region is a coexistence regime with both a and ß phases. The three points 1, 2 and 3 in the coexistence region are at 22.8 wt% A, 28.2 wt% A, and 33.7 wt % A respectively. If the points on the phase boundaries L and R are at 20 wt% A and 39 wt % A, respectively, what is the fraction of a phase at 1, 2 and 3? (This question has only one correct answer) T(°C) A-B binary alloy 1400 Coexistence region 3 1 2 1100 B 20 % 40 % Weight % A
For alloy A-B of composition Co (C dot) is 33 at some temperature is found to consist of mass fractions of 0.75 and 0.25 for alpha and beta phases respectively. If the composition of the alpha phase is 15wt% B - 85 wt% A, what is the composition of the beta phase?
According to the following graph, two samples of 1080 steel are cooled from the eutectoid temperature, one at a cooling rate of 250°C/s and the other at a cooling rate of 7.27x10-8 °C/s. Specify the phases obtained and explain their formation from thermodynamic and kinetic perspectives. Also, briefly describe their formation. Draw the microstructure of the phases obtained. Sıcaklık (C) 800 700 600 500 400 300 200 100 0 10 1 T M(başlama) M(% 50) M(% 90) 10 M+O -Otektoid Sıcaklık 10² Zaman (s) % 50 10³ 104 105
ASAP
Copper (Cu) and silver (Ag) alloys form a binary alloy system that dissolves each othercompletely in the liquid state but only partially soluble in each other in the solid state.- The melting point of Cu is 1080 C and the melting point of Ag is 960 C.- At a temperature of 790 C, a eutectic reaction occurs in the 72% Ag alloy. At this temperature, Cucapable of dissolving 10% Ag and its eutectic microstructure is known to have a ratio of /β = 7/19 (findthe point of solubility of Cu in Ag at the eutectic temperature).- At room temperature (25 C), Cu metal can dissolve 5% Ag while Ag metal candissolve 2% Cu.a. Draw a phase diagram of the alloy system complete with the names of points, lines and phase regions.b. The 80%Ag alloy is cooled in equilibrium.i. Draw the cooling curve from liquid to solid state, complete withtemperature, the phases at each stage and the reactions that occur.ii. At the eutectic temperature (4a before and 4b after the eutectic reaction), determine the…
In precipitation Duralumin, intermediate precipitates can hardenable alloy, like form due to a, difficulty of nucleation of the final precipitates b. difficulty of growth of the final precipitate с. ease of diffusion d. coherency strain
A copper-nickel alloy contains 38% by weight of Cu and 62% by weight of Ni and is at 1330 ° C. Using the figure, answer the following questions:a) What is the percentage by weight of copper in the solid and liquid phases at this temperature?b) What percentage by weight of the alloy is liquid and what percentage is solid?