Consider 0.60 kg of austenite containing 1.3 wt% C, cooled to below 727°C (1341°F). Using the iron-iron carbide phase diagram,Animated Figure 9.24, determine the following:(a) How many kilograms of total ferrite formikg(b) How many kilograms of total cementite formikg(c) How many kilograms of pearlite formkg(d) How many kilograms of the proeutectoid phase formikg Temperature (°C)1600140012001000800600400(Fe)0(0)1538 °C1394 °C-1493 °Ca+yy, Austenite912 °C0.760.022, Feritte5701085 °CV +L2Composition (at% C)10152.141147 °Ca + Fę. CLComposition = 0 wt% CComposition = 0 at% CTemperature = 400 °CTemperature = 752 °F34Composition (wt% C)4.30y + Fe3C727 °C20Cementite (Fe,C)5625250012000150010006.70Temperature (°F)

“Since you have posted a question with multiple sub-parts, we will provide the solution only to the…

Consider 0.60 kg of austenite containing 1.3 wt% C, cooled to below 727°C (1341°F). Using the iron-iron carbide phase diagram, Animated Figure 9.24, determine the following: (a) How many kilograms of total ferrite form i kg (b) How many kilograms of total cementite form i kg (c) How many kilograms of pearlite form i kg (d) How many kilograms of the proeutectoid phase form i kg

Consider 0.60 kg of austenite containing 1.3 wt% C, cooled to below 727°C (1341°F). Using the iron-iron carbide phase diagram, Animated Figure 9.24, determine the following: (a) How many kilograms of total ferrite form i kg (b) How many kilograms of total cementite form i kg (c) How many kilograms of pearlite form i kg (d) How many kilograms of the proeutectoid phase form i kg

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Consider 1.0 kg of austenite containing 1.15 wt% C, cooled to below 727 °C (1341 °F). (a) What is the proeutectoid phase? (b) How many kilograms each of total ferrite and cementite form? (c) How many kilograms each of pearlite and the proeutectoid phase form? (d) Schematically sketch and label the resulting microstructure. Temperature (°C) 1600 1400 1200 1000 800 600 1538°C 400 0 -1493°C 1394°C 912°C y, Austenite 0.76 0.022 a, Ferrite 5 Y+L 2.14 Composition (at% C) 15 10 1147°C a + Fe3C L 4.30 y + Fe3C 727°C 20 Cementite (Fe3C) 5 6 4 (Fe) Composition (wt% C) Adapted from Binary Alloy Phase Diagrams, Vol. 1, 2nd edition, T. B. Massalski (Editor-in-Chief), 1990. Reprinted by permission of ASM International, Materials Park, OH. 25 2500 2000 1500 -1000 6.70 Temperature (°F)
3. The figure below shows the phase diagram for a hypoeutectoid plain carbon steel. Assume that point c is slightly above 723 °C and point d is slightly below 723 °C. i. ii. iii. Explain the structure at points a, b, c, and d on the diagram. Determine the wt% of proeutectoid ferrite at point c. Determine the wt% of eutectoid ferrite at point d. Temperature (°C) 1000 900 800 700 600 500 400 0 100% Fe y+ a 0.02 a + Fe, C b 0.4 723°C y + Fe, C Pearlite 0.8 Weight percent carbon Fe₂C 6.67
1-The microstructural design of Iron-Carbon(Fe-C) alloys has led to the development of vast range of steels for structural material applications. The phase diagram provide means for producing specific microstructures. Using the phase diagram below to answer the following questions A – If the liquid mixture of Fe-3%Wt C is slowly cooled from 1600 C to 1200C indicate the phase(S) that are present at 1200 C . Also calculate the composition of the of phases.(10) B-Describe the sequence of all phase transformation that accour from Fe-1.5%wt C is slowly cooled from 1600 C to 400 C. Use the diagram below to to describe the microstructures for each phase transformation (10)
According to the following graph, two samples of 1080 steel are cooled from the eutectoid temperature, one at a cooling rate of 250°C/s and the other at a cooling rate of 7.27x10-8 °C/s. Specify the phases obtained and explain their formation from thermodynamic and kinetic perspectives. Also, briefly describe their formation. Draw the microstructure of the phases obtained. Sıcaklık (C) 800 700 600 500 400 300 200 100 0 10 1 T M(başlama) M(% 50) M(% 90) 10 M+O -Otektoid Sıcaklık 10² Zaman (s) % 50 10³ 104 105
For 40 wt% Sn – 60 wt% Pb alloy at 150 oC (at point B) as shown in Figure, i. State the name of phase(s) present. ii. Calculate the composition(s) of the phase(s) present. 600 300 Liquid 500 a+L 200 400 300 100 200 100 20 60 100 (Pb) (Sn) Composition (wt % Sn) Temperature ("C) Temperature ("F)
1.9 kg of austenite containing 1.50 Wt% C is cooled from 1200 degrees C to a temperature just below the eutectoid line. 1. What is the proeutectoid phase? 2. How many kilograms each of total ferrite and comentite form? 3. How many kilograms each of pearlite and the proeutectoid phase form?
4b) Figure 6 shows the Fe-Fe3C phase diagram. Evaluate (i) the temperature at which austenite first begins to transform on cooling; (ii) the primary microconstituent that forms; (iii) the composition and amount of each phase present at 728°C; (iv) the composition and amount of each phase present at 726°C; (v) Sketch the evolution of the microstructures of hypereutectoid steels with 1.1 wt% of carbon during the cooling in relationship to Fe-Fe3C phase diagram shown at 900°C, 800°C and 500°C, respectively.
A binary alloy having 28 wt% Cu and balance Ag solidifies at 779°C. The solid consists of two phases a and B. Phase a has 9% Cu whereas phase ß has 8 % Ag at 779°C. At room temperature these are pure Ag and Cu respectively Sketch the phase diagram. Label all phases and temperatures. The melting points of copper and silver are 1083 and 9610 respectively s Pà) Estimate the amount of a and B in the above alloy at 779°C and at room temperature.) b) Calculate the mass fraction of phases for 40% Cu alloy at 300 °C and TR c) What is the composition of the alloys in (b)
Question 2: For the given Fe-C phase duagram (a) Compute the mass fractions of a ferrite and cementite in pearlite. (b) Compute the mass fraction of eutectoid ferrite in an iron-carbon alloy that contains 0.43 wt% C. (c) The mass fractions of total ferrite and total cementite in an iron-carbon alloy are 0.88 and 0.12, respectively. Is this a hypoeutectoid or hypereutectoid alloy? Why? Temperature (°C) 1600 1400 1200 1000 800 600 400 1538°C (Fe) 912°C M+R -1493°C 1394°C 7. Austenite 0.76 0.022 a, Ferrite y+L 2 2.14 Composition (at% C) 15 10 1147°C a + FezC L 3 Composition (wt% C) 4.30 Y+Fe3C 727°C 20 Cementite (Fe3C). 25 2500 2000 1500 1000 6.70 Temperature (°F)
A hypo-eutectoid steel with composition of 0.5% carbon is heated to 1000°. Using the a iron-carbon phase diagram (also found in the course book, or here https://commons.wikimedia.org/wiki/File:Iron_carbon_phase_diagram.svg (Links to an external site.) (Links to an external site.)) answer the following questions. (a) What phase or phases will be present at 950°C? (b) If temperature is lowered from 950°C, at which temperature (estimate) α phase (Ferrite) will appear? (c) Use the lever rule to estimate how much (wt%) ferrite and how much austenite will exist just above 727 °C? (d) What happens to the austenite if the temperature is lowered below 727 °C? (e) Schematically sketch and label the resulting microstructure.
Figure below is a binary eutectic copper-silver phase diagram. Consider if 500 grams of an 88 wt% Ag–12 wt% Cu alloy is slowly cooled from 1000oC to 700oC. α-phase is copper-rich solid solution and β-phase is silver-rich solid solution. Density of copper and silver is 8.96 g/cm3 and 10.49 g/cm3 respectively. At 700oC, determine the: 1)composition of the phases present.
Using the following table, draw a melting point diagram and estimate the eutectic temperature and composition: Percent composition Melting point range (°C) 100% A 125-126 75% A-25% B 115-120 65% A- 35% B 128-131 50% A- 50% B 135-140 100% B 151-152 Can you suggest what additional points you need to give a more accurate measure of the eutectic point?