A cylindrical specimen of undeformed brass that has a diameter of 300 mm is elastically deformed to a tensile strain of 0.001. If the Poisson's ratio for this brass is 0.35, what is the change in specimen diameter? O Decrease by 3.00 x 10-4 m O Increase by 1.05 x 10-4 m O Increase by 0.028 mm O Decrease by 1.05 x 10-4 m

A cylindrical specimen of undeformed brass that has a diameter of 300 mm is elastically deformed to a tensile strain of 0.001. If the Poisson's ratio for this brass is 0.35, what is the change in specimen diameter? O Decrease by 3.00 x 10-4 m O Increase by 1.05 x 10-4 m O Increase by 0.028 mm O Decrease by 1.05 x 10-4 m

Mechanics of Materials (MindTap Course List)

9th Edition

ISBN:9781337093347

Author:Barry J. Goodno, James M. Gere

Publisher:Barry J. Goodno, James M. Gere

Chapter2: Axially Loaded Members

Section: Chapter Questions

Problem 2.7.5P: Determine the strain energy per unit volume (units of psi) and the strain energy per unit weight...

See similar textbooks

Similar questions

A cylindrical specimen of a steel alloy 10 mm in diameter and 100mm long is pulled in tension at a load of 23500N and the strain found to be 0.0015, the elongation will be: Select one: 0.15mm Ob. 0.023mm 0.100mm Od. 0.0015mm
A ul ? KBIS M 1:11 O photo_2021-0... -> 200 stress 150 (MPa) (00 50 0-2 strain From the tensile stress-strain behavior for the brass specimen d the diamcter is 12-8 mm Calculate the folluding:- 1- The Yield stress. 2- Modulus of elasticity. 3 - The Tensile strength . II
A tensile force of 10 kN is applied on a 0.02-m diameter and 2-m long rod. After applying theload, the diameter of the rod decreases to 0.01998 m and the length increases to 2.01 m. The lateral (transverse) strain is?
In our previous topic regarding strain, repeat the problem on the strain using thefollowing parameters:F = 150000 +/- 150 lbfSide length = 1.2 +/- 0.025 inModulus of Elasticity = 25000 +/- 11.5 ksiDetermine the relative error. Is it above or below the accepted 5% error?
True stress-strain Engineering stress-strain strain Calculate the engineering ultimate tensile strength of a material whose strength coefficient is 535 MPa and of a tensile-test specimen that necks at a true strain of 0.55. 200 MPa O 267 MPa O 244 MPa O 222 MPa stress
The relationship between true strain (ɛ-) and engineering strain (ɛ) in a uniaxial tension test is given as (a) & = In (1 + &7) (c) &7= In (1+ E) (b) ɛg = In (1- E) (d)= in (1- E) %3D %3D
200 stress 150 (MPa) 100 50 0-2 strain From the tensile stress-strain behavior for the brass specimen cP the diameter is 12-8 mm Calculate the folwing:- 1- The Yield stress, 2-Modulus of elasticity. 3- The Tensile strength .
The data below are for a thin steel wire suitable for use as a guitar string. Ultimate tensile stress: 1.8 x 109 Pa Young Modulus: 2.2 x 1011 Pa Cross-sectional area: 2.0 x 10-7 m2 In a tensile test, a specimen of the wire, of original length 1.5 m, is stretched until it breaks. Assuming the wire obeys Hooke’s law throughout, calculate the extension of the specimen immediately before breaking.
Consider an aluminum specimen with a diameter of 10 mm and a length of 1 point 3 m. A force of 3000 N is applied along the axis of each specimen. Assuming that the deformation is elastic, estimate the elongation of the specimen. Aluminum (E-70 GPa)
A man leg can be thought of as a shaft of bone 1.2 m long. If the strain is 1.3x10-4 when the leg supports his weight, by how much is his leg shortened?
. From the tensile stress-strain behaviour for a casted iron as shown in the following curve. Please answer the following questions (1) Estimate the modulus of elasticity, (2) Calculate the change in length of a specimen with original length of 100mm that is subjected to a tensile stress of 300MPa. (Hint: Using the Hooke's law to get the strain.) 600 500 400 - 300 - 200 - 100 - 2 4 6. 8 10 12 14 16 Strain Strength (MPa)
A material has a linear elastic perfectly plastic stress-strain. A cylindrical specimen of that material having an initial length of 35 mm and a tadius of 7 mm is pulled until it elongates 0.8mm. a. Calculate the stain and the corresponding stress at that elongation value. b. Afterward, the specimen is released to zero stress level, how does the final length of the specimen compare with its original length? How much plastic deformation remains if it exists?