A 250 mm wide strip of 20 mm thickness is reduced to 18 mm in a single pass through a rolling process. the radius of each roller is 200 mm and its speed is 150 RPM. The strength coefficient for work material is 280 N/mm and the value of strain hardening coefficient is 0.15. The coefficient of friction between the workpiece and the rolls is 0.12. Find the roll force, torque and power required per roll.

A 250 mm wide strip of 20 mm thickness is reduced to 18 mm in a single pass through a rolling process. the radius of each roller is 200 mm and its speed is 150 RPM. The strength coefficient for work material is 280 N/mm and the value of strain hardening coefficient is 0.15. The coefficient of friction between the workpiece and the rolls is 0.12. Find the roll force, torque and power required per roll.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A 42mm thick low carbon steel plate is reduced to 34mm in one rolling pass. At the same time that the thickness is reduced, the plate is widened by 4%. The elastic limit of the steel plate is 174MPa and its resistance is 290MPa. The input speed of the plate is 15m/min. The radius of the cylinder is 52.8mm and the rotation speed is 49 revolutions per minute. Determine: a) The minimum coefficient of friction that will make this rolling operation possible. b) The output speed of the plate c) Slide forward
Thickness of the plate is reduced from 40mm to 20mm by succesive cold rolling passes using identical rolls of diameter 600 mm. Assume that there is no change in width. If the coefficient of friction b/w the rolls and the workpiece is 0.1. Determine the minimum number of passes required?
A solid piece of steel 60 mm in diameter and 80 mm height is reduced in height by 50 percent with the help of open die forging. The work material characteristics are represented by k = 350MPA and n = 0.16. If coefficient of friction is 0.1, find the maximum forging force.
Please give me full explanation in 1hour do it fast A 4-in-thick aluminum slab is 10 in wide and 100 in long. It is reduced in one pass in a two-high rolling mill to a thickness = 3.5 in. The roll rotates at a speed = 12 rev/min and has a radius = 20 in. The aluminum has a strength coefficient = 25,000 lb/in2 and a strain hardening exponent = 0.20. Determine the (a) roll force, (b) roll torque, and (c) power required to accomplish this operation, d) Estimate the GHG emission in an hour for the rolling operation.
A mechanical press is powered by a 23-kW motor and operates at 40 strokes per minute. It uses a flywheel, so that the crankshaft speed does not vary appreciably during the stroke. If the stroke is 150 mm, what is the maxumum const.ant force rhat can be exerted over the entire stroke length?
Two high rolling mill setup has been used to reduce the thickness of a plate from 40 mm at the maximum draft per pass to become 34 mm after the last pass. The width of the rolled material is 560 mm and the roll diameter is 560 mm. The material has a strength coefficient of 260 MPa and a strain hardening exponent of 0.18. The coefficient of friction during the process was 0.085. Determine the following: 1- Number of passes required to perform the reduction process = 2- Strain of the last pass = 3- Average flow stress of the last pass = MPa 4- The rolling force to roll the last pass =
(c) A flat rolling operation is being carried out where the roll radius is 200 mm and the roll rotates at 100 rpm. The workpiece material is annealed low carbon steel with 200 mm wide and 10 mm thickness. The strength coefficient and the strain hardening of the carbon steel are 530 MPa and 0.26, respectively. The coefficient of friction is 0.2. (i) Caicurae tne roll force and torque if the workpiece is rolled to a thickness of 4 mm. (ii) Calculate the maximum possible draft and evaluate how friction effect the thickness of the rolled workpiece.
A 300-mm-wide strip 25-mm thick is fed (Bottom roll removed) through a rolling mill with two powered Roll No-slip point rolls each of radius = 250 mm. The work %3D Workpiece- thickness is to be reduced to 22 mm in Friction forces one pass at a roll speed of 50 rev/min. The Entry Roll Exit Torque zone gap, L zone work material has a flow curve defined by K=275 MPa and n 0.15, and the coefficient of friction between the rolls and the work is %3D assumed to be 0.12. Determine if the friction is sufficient to permit the rolling operation to be accomplished. If so, calculate the roll force, torque, and horsepower.
Walk-Through Video Dashboard Note: - You are attempting question 4 out of 12 In a rolling operation, a plate of 2 cm thick and 25 cm wide is passed through a rolling mill having 2 powered rolls. Assume friction was enough for rolling. Thickness of the plate at the end of operation is 1.7 cm. Each roll has a radius of 0.3 m and a roll speed of 0.5 revolution per second. Flow curve has the following values K = 225 MPa and n = 0.15. Determine the power required for driving the rolls.
A wire is drawn through a draw die with an entry angle = 15o. The starting diameter is 0.100 in. And the final diameter = 0.080 in. The coefficient of friction at the work-given interface = 0.07. The metal has a coefficient of resistance K = 30,000 psi and a strain hardening exponent of n = 0.20. Determine the stretching force and the stretching force in this operation.
In a single pass rolling bearing process using 510mm diameter steel rollers a strip of width 110mm and thickness 6mm undergoes 20%reduction of thickness. Find the angle of bite
the work metal has a flow curve defined by K=300MPa and n=0.2, and the coefficient of friction between the rolls and the work is assumed to be 0.1. a 250mm wide strip 2.0cm thick is fed through a rolling mill with two powered rolls each of radius=300mm. the work thickness is to be reduced to 18mm in one pass at a roll speed of 50rev/min. what will be the power for this operation?